The effect of hydrogen charging on the mechanical properties of leaded α/β brass cast alloy

被引:2
|
作者
Panagopoulos, C. N. [1 ]
Giannakopoulos, K. I. [2 ]
机构
[1] Natl Tech Univ Athens, Met Phys Lab, Athens 15780, Greece
[2] Piraeus Univ Appl Sci, Lab Strength Mat, Athens 12244, Greece
来源
MATERIALIA | 2019年 / 5卷
关键词
Brass; Hydrogen embrittlement; Diffusion; Fick's law; Metal hybrid; mechanical properties; Tensile; SPONTANEOUS DISSOLUTION; FRACTURE PROCESSES; INDUCED CRACKING; COPPER HYDRIDE; DEFORMATION; BEHAVIOR; EMBRITTLEMENT; POROSITY; STRESS; NICKEL;
D O I
10.1016/j.mtla.2018.100184
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
At the present work, the effect of the cathodic charging on the mechanical properties of leaded alpha/beta brass cast alloy was investigated. The charging conditions of the test samples were as follows: current density: (a) 5 mA/cm(2), (b) 20 mA/cm(2), (c) 40 mA/cm(2) and (d) 55 mA/cm(2). The durations of the charging of the test samples were (a) 5 h, (b) 10 h, (c) 15 h, (d) 25 h and (e) 50 h. For the samples that underwent tensile stress at three different rates of loading, the following conditions of hydrogen cathodic charging were selected: current density: 20 mA/cm(2) with charging time of (a) 5 h, (b) 20 h and (c) 40 h. All of the samples were subjected to tensile stress tests with a constant deformation rate of 10(-4)sec(-1). The main conclusions for the above investigation are that the average value of the microhardness of the surface of the cathodically charged test samples was found to increase with the increase in the current density of cathodic charging at a constant value of cathodic charging time and with the increase of the cathodic charging time at a constant value of current density, in addition to an decrease of the microhardness value of the cathodically charged test samples with increased distance from the test sample's surface. The maximum width of the affected area, under the conditions of the experiment, was 550 mu m. The ductility of the cathodically charged test samples was notably reduced compared to that of the uncharged material, compared to the uncharged material.
引用
收藏
页数:8
相关论文
共 50 条
  • [21] Effect of suction cast on structure and hydrogen storage properties of TiVCr based alloy
    Zhang Jinlong
    Jin Hangjun
    Lin Genwen
    Fang Shoushi
    Li Xiaochun
    Ge Hansheng
    RARE METAL MATERIALS AND ENGINEERING, 2007, 36 (03) : 398 - 401
  • [22] EFFECT OF HYDROGEN GAS ON THE MECHANICAL-PROPERTIES OF A ZIRCONIUM ALLOY
    HUANG, JH
    HO, CS
    MATERIALS CHEMISTRY AND PHYSICS, 1994, 38 (02) : 138 - 145
  • [23] Influence of ECAP processing on mechanical and wear properties of brass alloy
    Radhi, Hussein Naser
    Mohammed, Mohsin Talib
    Aljassani, Alaa M. H.
    MATERIALS TODAY-PROCEEDINGS, 2021, 44 : 2399 - 2402
  • [24] Investigation of fracture mechanical properties of a brass alloy with microstructural variations
    Klaushofer, Martin Benedikt
    Stoschka, Michael
    Maier, Bernd
    Gruen, Florian
    ENGINEERING FRACTURE MECHANICS, 2024, 311
  • [25] Effect of pouring temperature on properties of cast red brass.
    不详
    JOURNAL OF THE FRANKLIN INSTITUTE, 1940, 229 : 106 - 106
  • [26] Effect of Boron Addition on Thermal and Mechanical Properties of Cast ZA 12 Alloy
    Ayday, Aysun
    Kurnaz, S. Can
    Uysal, Unal
    Pehlivan, Huseyin
    INTERNATIONAL JOURNAL OF METALCASTING, 2023, 17 (01) : 1 - 12
  • [27] Effect of Boron Addition on Thermal and Mechanical Properties of Cast ZA 12 Alloy
    Aysun Ayday
    S. Can Kurnaz
    Ünal Uysal
    Hüseyin Pehlivan
    International Journal of Metalcasting, 2023, 17 : 1 - 12
  • [28] Effect of carbon on the microstructures and mechanical properties of as cast Nb-base alloy
    Ding, Rengen
    Jones, Ian P.
    Jiao, Huisheng
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 485 (1-2): : 92 - 98
  • [29] Effect of additional Sb on the properties of the corrosion - resistance of cast brass
    Liu, Gang
    Huang, Liangyu
    Zhuzao/Foundry, 1988, (12): : 19 - 21
  • [30] The Effect of Iron Content on Microstructure and Mechanical Properties of A356 Cast Alloy
    Tansel Tunçay
    Samet Bayoğlu
    Metallurgical and Materials Transactions B, 2017, 48 : 794 - 804