Stress corrosion cracking behaviour of a surface-modified magnesium alloy

被引：42
|
作者：
Srinivasan, P. Bala [1 ]
Blawert, C. [1 ]
Dietzel, W. [1 ]
Kainer, K. U. [1 ]
机构：
[1] GKSS Forschungszentrum Geesthacht GmbH, Inst Mat Res, D-21502 Geesthacht, Germany
来源：
SCRIPTA MATERIALIA | 2008年 / 59卷 / 01期
关键词：
magnesium alloy; plasma electrolytic oxidation; microstructure; electrochemical behaviour; stress corrosion cracking;
D O I：
10.1016/j.scriptamat.2008.02.032
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The effect of plasma electrolytic oxidation (PEO) treatment on the stress corrosion cracking (SCC) of a cast magnesium alloy was assessed. Even though the PEO coating has offered improved corrosion resistance, as evidenced in electrochemical tests, its effect in improving the SCC resistance in ASTM D1384 test solution was only marginal. The SCC behaviour of PEO-coated specimens was attributed to the development of microcracks in the coating, leading to cracking of the substrate under slow strain rate test conditions. (C) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：43 / 46
页数：4
相关论文
共 50 条
  • [21] Stress Corrosion Cracking of Magnesium Alloys
    Atrens, Andrej
    Winzer, Nicholas
    Dietzel, Wolfgang
    ADVANCED ENGINEERING MATERIALS, 2011, 13 (1-2) : 11 - 18
  • [22] Influence of bovine serum albumin in Hanks' solution on the corrosion and stress corrosion cracking of a magnesium alloy
    Harandi, Shervin Eslami
    Banerjee, Parama Chakraborty
    Easton, Christopher D.
    Raman, R. K. Singh
    MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2017, 80 : 335 - 345
  • [23] Effect of plasma electrolytic oxidation coating on the stress corrosion cracking behaviour of wrought AZ61 magnesium alloy
    Srinivasan, P. Bala
    Blawert, C.
    Dietzel, W.
    CORROSION SCIENCE, 2008, 50 (08) : 2415 - 2418
  • [24] Fatigue Behaviour of Cast Aluminium Alloy Surface-Modified by Friction Stir Surface Processing
    Uematsu, Yoshihiko
    Tokaji, Keiro
    Tozaki, Yasunari
    STEEL RESEARCH INTERNATIONAL, 2010, 81 (09) : 1084 - 1087
  • [25] Inhibiting stress corrosion cracking of a prefabricated surface-defective magnesium alloy thanks to biological organic components
    Chen, Lianxi
    Li, Xiaorong
    Gu, Haicheng
    Zhang, Xueying
    Niu, Ben
    Zhang, Zhiguo
    Wang, Xiaojian
    Chen, Dongchu
    Zhao, Chunwang
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, 47 (07) : 2441 - 2463
  • [26] CORROSION PROPERTIES OF SURFACE-MODIFIED MATERIALS
    MELETIS, EI
    HOCHMAN, RF
    JOURNAL OF METALS, 1987, 39 (12): : 25 - 27
  • [27] Corrosion behaviour of the microbially modified surface of 5083 aluminium alloy
    Nkoua, C.
    Josse, C.
    Proietti, A.
    Basseguy, R.
    Blanc, C.
    CORROSION SCIENCE, 2023, 210
  • [28] Stress corrosion cracking behaviour of excimer laser treated aluminium alloy 6013
    Xu, W. L.
    Yue, T. M.
    Man, H. C.
    MATERIALS TRANSACTIONS, 2008, 49 (08) : 1836 - 1843
  • [29] Effect of laser shock processing on stress corrosion cracking behaviour of AZ31 magnesium alloy at slow strain rate
    Li, X. C.
    Zhang, Y. K.
    Chen, J. F.
    Lu, Y. L.
    MATERIALS SCIENCE AND TECHNOLOGY, 2013, 29 (05) : 626 - 630
  • [30] Stress corrosion cracking of magnesium alloys: A review
    Jiahao Jiang
    Xue Geng
    Xiaobo Zhang
    Journal of Magnesium and Alloys, 2023, (06) : 1906 - 1930
12345