Stress corrosion cracking behaviour of a surface-modified magnesium alloy

被引：42
|
作者：
Srinivasan, P. Bala [1 ]
Blawert, C. [1 ]
Dietzel, W. [1 ]
Kainer, K. U. [1 ]
机构：
[1] GKSS Forschungszentrum Geesthacht GmbH, Inst Mat Res, D-21502 Geesthacht, Germany
来源：
SCRIPTA MATERIALIA | 2008年 / 59卷 / 01期
关键词：
magnesium alloy; plasma electrolytic oxidation; microstructure; electrochemical behaviour; stress corrosion cracking;
D O I：
10.1016/j.scriptamat.2008.02.032
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The effect of plasma electrolytic oxidation (PEO) treatment on the stress corrosion cracking (SCC) of a cast magnesium alloy was assessed. Even though the PEO coating has offered improved corrosion resistance, as evidenced in electrochemical tests, its effect in improving the SCC resistance in ASTM D1384 test solution was only marginal. The SCC behaviour of PEO-coated specimens was attributed to the development of microcracks in the coating, leading to cracking of the substrate under slow strain rate test conditions. (C) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：43 / 46
页数：4
相关论文
共 50 条
  • [1] Stress corrosion cracking behaviour of a surface modified magnesium alloy (vol 59, pg 43, 2008)
    Srinivasan, P. Bala
    Blawert, C.
    Dietzel, W.
    Kainer, K. U.
    SCRIPTA MATERIALIA, 2009, 60 (10) : 924 - 924
  • [2] Corrosion properties of surface-modified AZ91D magnesium alloy
    He Meifeng
    Liu Lei
    Wu Yating
    Tang Zhixin
    Hu Wenbin
    CORROSION SCIENCE, 2008, 50 (12) : 3267 - 3273
  • [3] Behavior of stress corrosion cracking in a magnesium alloy
    Renguo Song
    Fanger Yang
    Carsten Blawert
    Wolfgang Dietzel
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2009, 24 : 111 - 113
  • [4] STRESS-CORROSION CRACKING OF MAGNESIUM ALLOY
    LOGAN, HL
    UGANISKY, GM
    STIEFEL, W
    ASM TRANSACTIONS QUARTERLY, 1966, 59 (03): : 586 - &
  • [5] Behavior of Stress Corrosion Cracking in a Magnesium Alloy
    宋仁国
    Journal of Wuhan University of Technology(Materials Science), 2009, (01) : 111 - 113
  • [6] Behavior of stress corrosion cracking in a magnesium alloy
    Song Renguo
    Yang Fanger
    Blawert, Carsten
    Dietzel, Wolfgang
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2009, 24 (01): : 111 - 113
  • [7] Corrosion characteristics of surface-modified DET magnesium powders
    Chung, WS
    Yoon, WY
    Kim, KJ
    DESIGNING, PROCESSING AND PROPERTIES OF ADVANCED ENGINEERING MATERIALS, PTS 1 AND 2, 2004, 449-4 : 369 - 372
  • [8] Corrosion behaviour and in vitro/in vivo biocompatibility of surface-modified AZ31 alloy
    Carboneras, M.
    Iglesias, C.
    Perez-Maceda, B. T.
    del Valle, J. A.
    Garcia-Alonso, M. C.
    Alobera, M. A.
    Clemente, C.
    Rubio, J. C.
    Escudero, M. L.
    Lozano, R. M.
    REVISTA DE METALURGIA, 2011, 47 (03) : 212 - 223
  • [9] Corrosion, stress corrosion cracking and corrosion fatigue behavior of magnesium alloy bioimplants
    Das, Priyabrata
    Kumar, T. S. Sampath
    Sahu, Kisor K.
    Gollapudi, Srikant
    CORROSION REVIEWS, 2022, 40 (04) : 289 - 333
  • [10] Hydrogen behaviour during stress-corrosion cracking of an AZ31 magnesium alloy
    Kuramoto, S.
    Araki, I.
    Kanno, M.
    Keikinzoku/Journal of Japan Institute of Light Metals, 2001, 51 (08): : 397 - 402
12345