Reaction Products of MgO and Microsilica Cementitious Materials at Different Temperatures

被引：50
|
作者：
Wei Jiangxiong [1 ]
Yu Qijun [1 ]
Zhang Wensheng [2 ]
Zhang Hongtao [2 ]
机构：
[1] S China Univ Technol, Sch Mat Sci & Engn, Guangzhou 510640, Guangdong, Peoples R China
[2] China Bldg Mat Acad, Res Inst Cement & New Bldg Mat, Beijing 100024, Peoples R China
来源：
JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION | 2011年 / 26卷 / 04期
关键词：
MgO; microsilica; magnesium silicate hydrate (M-S-H); MAGNESIUM-SULFATE ATTACK; SILICATE; PASTE;
D O I：
10.1007/s11595-011-0304-3
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The paste was prepared by mixing MgO, microsilica and H2O in the presence of water reducer at different reaction ratios and temperatures, and characterized by XRD, DTA, TGA, IR, and solid-state 29Si NMR. The experimental results showed that, besides Mg(OH)(2), magnesium silicate hydrate (M-S-H) was formed at a low temperature such as 25 and 50 degrees C. At a high temperature of 100 degrees C, Mg(OH)(2) can be further transformed into M-S-H completely, for instance, within ca. 1 month in an excess of microsilica. The average composition and structure of M-S-H was mainly related to the reaction mixture and curing temperature and was discussed in detail.
引用
收藏
页码：745 / 748
页数：4
相关论文
共 50 条
  • [1] Reaction products of MgO and microsilica cementitious materials at different temperatures
    Jiangxiong Wei
    Qijun Yu
    Wensheng Zhang
    Hongtao Zhang
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2011, 26 : 745 - 748
  • [2] Reaction Products of MgO and Microsilica Cementitious Materials at Different Temperatures
    韦江雄
    Journal of Wuhan University of Technology(Materials Science Edition), 2011, 26 (04) : 745 - 748
  • [3] Reaction Products of MgO and Microsilica Cementitious Materials at Different Temperatures
    韦江雄
    Journal of Wuhan University of Technology(Materials Science), 2011, (04) : 745 - 748
  • [4] The Reaction Mechanism between MgO and Microsilica at Room Temperature
    韦江雄
    JournalofWuhanUniversityofTechnology(MaterialsScienceEdition), 2006, (02) : 88 - 91
  • [5] Reaction mechanism between MgO and microsilica at room temperature
    Wei J.
    Chen Y.
    Li Y.
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2006, 21 (2): : 88 - 91
  • [6] The reaction mechanism between MgO and microsilica at room temperature
    Wei Jiangxiong
    Chen Yimin
    Li Yongxin
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2006, 21 (02): : 88 - 91
  • [7] Physicochemical properties of MgO-silica fume cementitious materials exposed to high temperatures
    Ma, Hongqiang
    Zhang, Shaochen
    Feng, Jingjing
    JOURNAL OF BUILDING ENGINEERING, 2022, 50
  • [8] Mechanical and microstructural property evolutions of MgO-slag cementitious materials under high temperatures
    Ma, Hongqiang
    Niu, Xiaoyan
    Feng, Jingjing
    JOURNAL OF BUILDING ENGINEERING, 2022, 56
  • [9] Effectiveness of 3 different supplementary cementitious materials in mitigating alkali silica reaction
    Meesak, Thanawat
    Sujjavanich, Suvimol
    MATERIALS TODAY-PROCEEDINGS, 2019, 17 : 1652 - 1657
  • [10] Analysis of Mortar Long-Term Strength with Supplementary Cementitious Materials Cured at Different Temperatures
    Ezziane, Karim
    Kadri, El-Hadj
    Bougara, Abdelkader
    Bennacer, Rachid
    ACI MATERIALS JOURNAL, 2010, 107 (04) : 323 - 331
12345