Development of thermal fatigue damage in 1CrMoV rotor steel

被引：48

作者：

Holdsworth, S. R. ^{[1
]}

Mazza, E. ^{[1
,2
]}

Binda, L. ^{[1
]}

Ripamonti, L.

机构：

[1] Empa, Swiss Fed Labs Mat Testing & Res, Lab Mech Modelling & Simulat, CH-8600 Dubendorf, Switzerland

[2] ETH, Inst Mech Syst, CH-8092 Zurich, Switzerland

来源：

NUCLEAR ENGINEERING AND DESIGN | 2007年 / 237卷 / 24期

关键词：

D O I：

10.1016/j.nucengdes.2007.05.002

中图分类号：

TL [原子能技术]; O571 [原子核物理学];

学科分类号：

0827 ; 082701 ;

摘要：

Crack initiation endurances have been determined for a 1CrMoV rotor steel in uniaxial service cycle thermo-mechanical fatigue (TMF) tests formulated to simulate a range of steam turbine start cycles with a maximum temperature of 565 degrees C. The experimental details for these TMF tests are described. Post test inspection has been employed to characterise the associated thermal fatigue damage mechanisms for the steel which are observed to be dependent on the magnitude of the thermal transient in the TMF cycle. The lowest resistance to thermal fatigue damage development occurs in these tests when the conditions determine that the rate of creep damage accumulation below the surface exceeds the rate of fatigue crack development at the surface. (C) 2007 Elsevier B.V. All rights reserved.

引用

页码：2292 / 2301

页数：10

共 16 条

[11]

MAYER KH, 1979, P INT DVM S LOW CYCL, P105

[12] Notched specimens thermo-mechanical fatigue of a 1CrMoV turbine steel [J].