Development of thermal fatigue damage in 1CrMoV rotor steel

被引：48

作者：

Holdsworth, S. R. ^{[1
]}

Mazza, E. ^{[1
,2
]}

Binda, L. ^{[1
]}

Ripamonti, L.

机构：

[1] Empa, Swiss Fed Labs Mat Testing & Res, Lab Mech Modelling & Simulat, CH-8600 Dubendorf, Switzerland

[2] ETH, Inst Mech Syst, CH-8092 Zurich, Switzerland

来源：

NUCLEAR ENGINEERING AND DESIGN | 2007年 / 237卷 / 24期

关键词：

D O I：

10.1016/j.nucengdes.2007.05.002

中图分类号：

TL [原子能技术]; O571 [原子核物理学];

学科分类号：

0827 ; 082701 ;

摘要：

Crack initiation endurances have been determined for a 1CrMoV rotor steel in uniaxial service cycle thermo-mechanical fatigue (TMF) tests formulated to simulate a range of steam turbine start cycles with a maximum temperature of 565 degrees C. The experimental details for these TMF tests are described. Post test inspection has been employed to characterise the associated thermal fatigue damage mechanisms for the steel which are observed to be dependent on the magnitude of the thermal transient in the TMF cycle. The lowest resistance to thermal fatigue damage development occurs in these tests when the conditions determine that the rate of creep damage accumulation below the surface exceeds the rate of fatigue crack development at the surface. (C) 2007 Elsevier B.V. All rights reserved.

引用

页码：2292 / 2301

页数：10

共 16 条

[1]

*ASTM, 2004, E2368 ASTM

[2]

BHONGBHIBHAT S, 1979, UNTERSUCHUNGEN WERKS

[3]

Bicego V., 1988, ASTM STP, V942, P1237

[4] Simple modelling of the constitutive behaviour of a 1%CrMoV rotor steel in service-like thermo-mechanical fatigue tests [J].

Colombo, F ;

Masserey, B ;

Mazza, E ;

Holdsworth, SR .

MATERIALS AT HIGH TEMPERATURES, 2002, 19 (04) :225-233

[5]

DAWSON RAT, 1989, P INT C MOD POW STAT

[6]

Harkegard G., 1992, HIGH TEMPERATURE STR, P21

[7]

Holdsworth SR, 2004, J TEST EVAL, V32, P255

[8]

Holdsworth SR, 1996, LIFE ASSESSMENT AND LIFE EXTENSION OF ENGINEERING PLANT, STRUCTURES AND COMPONENTS, P137

[9]

Lemaitre J, 1994, MECH SOLID MAT

[10] Factors influencing the service-like thermomechanical fatigue test cycle endurance of 1% CrMoV rotor steel [J].

Masserey, B ;

Colombo, F ;

Mazza, E ;

Holdsworth, S .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2003, 26 (11) :1041-1052

← 1 2 →