Effect of neutron irradiation on select MAX phases

被引:195
作者
Tallman, Darin J. [1 ]
Hoffman, Elizabeth N. [2 ]
Caspi, El'ad N. [1 ]
Garcia-Diaz, Brenda L. [2 ]
Kohse, Gordon [3 ]
Sindelar, Robert L. [2 ]
Barsoum, Michel W. [1 ]
机构
[1] Drexel Univ, Dept Mat Sci & Engn, Philadelphia, PA 19104 USA
[2] Savannah River Natl Lab, Savannah, SC 29808 USA
[3] MIT, Nucl Reactor Lab, Cambridge, MA 02139 USA
关键词
Ti2AlC; Ti3SiC2; Ti3AlC2; Neutron irradiation; Rietveld refinement; TI3SIC2; TEMPERATURE; TI3ALC2; OXIDATION; NUCLEAR; TI2ALC; DAMAGE; CONDUCTIVITY; TOLERANCE; EVOLUTION;
D O I
10.1016/j.actamat.2014.10.068
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Herein we report on the effect of neutron irradiation - of up to 0.1 displacements per atom at 360(20)degrees C or 695(25)degrees C - on polycrystalline samples of Ti3AlC2, Ti2AlC, Ti3SiC2 and Ti2AlN. Rietveld refinement of X-ray diffraction patterns of the irradiated samples showed irradiation-enhanced dissociation into TiC of the Ti3AlC2 and Ti3SiC2 phases, most prominently in the former. Ti2AlN also showed an increase in TiN content, as well as Ti4AlN3 after irradiation. In contrast, Ti2AlC was quite stable under these irradiation conditions. Dislocation loops are seen to form in Ti2AlC and Ti3AlC2 after irradiation at 360(20)degrees C. The room temperature electrical resistivity of all samples increased by an order of magnitude after irradiation at 360(20)degrees C, but only by 25% after 695(25)degrees C, providing evidence for the MAX phases' dynamic recovery at temperatures as low at 695(25)degrees C. Based on these preliminary results, it appears that Ti2AlC and Ti3SiC2 are the more promising materials for high-temperature nuclear applications. (C) 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码:132 / 143
页数:12
相关论文
共 43 条
[1]  
[Anonymous], 2010, CERAMICS SCI TECHNOL
[2]  
Barsoum M.W., 2004, Encyclopedia of Materials: Science and Technology, P1, DOI DOI 10.1016/B0-08-043152-6/01931-8
[3]   Electrical conductivity, thermopower, and hall effect of Ti3AIC2, Ti4AIN3, and Ti3SiC2 [J].
Barsoum, MW ;
Yoo, HI ;
Polushina, IK ;
Rud, VY ;
Rud, YV ;
El-Raghy, T .
PHYSICAL REVIEW B, 2000, 62 (15) :10194-10198
[4]   The topotactic transformation of Ti3SiC2 into a partially ordered cubic Ti(C0.67Si0.06) phase by the diffusion of Si into molten cryolite [J].
Barsoum, MW ;
El-Raghy, T ;
Farber, L ;
Amer, M ;
Christini, R ;
Adams, A .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1999, 146 (10) :3919-3923
[5]   Processing and characterization of Ti2AlC, Ti2AlN, and Ti2AlC0.5N0.5 [J].
Barsoum, MW ;
Ali, M ;
El-Raghy, T .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (07) :1857-1865
[6]  
Barsoum MW, 2013, MAX PHASES: PROPERTIES OF MACHINABLE TERNARY CARBIDES AND NITRIDES, P1, DOI 10.1002/9783527654581
[7]   Long-Term Oxidation of Ti2AlC in Air andWater Vapor at 1000-1300°C Temperature Range [J].
Basu, S. ;
Obando, N. ;
Gowdy, A. ;
Karaman, I. ;
Radovic, M. .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2012, 159 (02) :C90-C96
[8]   Contribution of core-loss fine structures to the characterization of ion irradiation damages in the nanolaminated ceramic Ti3AlC2 [J].
Bugnet, M. ;
Mauchamp, V. ;
Eklund, P. ;
Jaouen, M. ;
Cabioc'h, T. .
ACTA MATERIALIA, 2013, 61 (19) :7348-7363
[9]   Stability of the nitrogen-deficient Ti2AlN x MAX phase in Ar2+-irradiated (Ti,Al)N/Ti2AlN x multilayers [J].
Bugnet, M. ;
Cabioc'h, T. ;
Mauchamp, V. ;
Guerin, Ph. ;
Marteau, M. ;
Jaouen, M. .
JOURNAL OF MATERIALS SCIENCE, 2010, 45 (20) :5547-5552
[10]  
Carpenter DavidMichael., 2010, An assessment of silicon carbide as a cladding material for light water reactors