Experiment of enhancing critical current in Bi-2223/Ag tape by means of ferromagnetic shielding

Critical current in multifilamentary Ag-sheath Bi-2223 tape is enhanced to some extent by means of thin and narrow coating of pure nickel. The concept of enhancing critical current is based on the magnetic shielding effect resulting in redirection of self-field flux lines. The Ni coating was introduced at the edge regime of the tape in order to redirect the perpendicular component of self-field lines which is severe at the edges. Critical current in a typical Ag-sheath Bi-2223 tape was enhanced Lip to similar to 11 % by 50 mu m thick and 0.4 mm long Ni coating Without any change of self-field loss. This fact reveals that additional ferromagnetic loss could be compensated by the shielding effect and increased critical current of the tape. The degree of enhancement in critical current as well as ferromagnetic impact on ac losses depend on the length and thickness of ferromagnetic coating introduced. Therefore, it is very important to control the geometry of ferromagnetic coating in order to balance the critical current and ac loss for optimum superconductor performance. Introduction of ferrornagnetic coating and its effect on electromagnetic properties in inultifilarnentary Bi-2223/Ag tape will be reported in this article. (c) 2005 Elsevier B.V. All rights reserved.