Modeling of grain size in superalloy IN718 during hot deformation

被引:24
作者
Zhang, JM [1 ]
Gao, ZY
Zhuang, JY
Zhong, ZY
机构
[1] Wright State Univ, Dept Mech & Mat Engn, Dayton, OH 45435 USA
[2] Cent Iron & Steel Res Inst, Dept Superalloys, Beijing 100081, Peoples R China
关键词
IN718; hot deformation; microstructure; modeling;
D O I
10.1016/S0924-0136(98)00401-4
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The microstructure and mechanical properties of IN718 forgings are highly sensitive to metallurgical technology and thermomechanical processing. To obtain the most favorable mechanical properties and microstructures in IN718 forgings, it is necessary to further understand the microstructure variation behavior and to be able to predict the grain size of superalloy IN718 during hot deformation. On the basis of isothermal constant-speed compression tests conducted using a computer-controlled MTS machine at temperatures from 960-1040 degrees C, with initial strain rates from 0.001-1.0 s(-1), to engineering strains from 0.1-0.7, the microstructure variation behavior of superalloy IN718 has been studied. Two different types of microstructures were found at deformation temperatures below and above 1000 degrees C. The effect of hot-deformation parameters on the microstructures was analyzed and a model was developed to describe the duplex microstructure and to express the relationship between the grain size and the hot-deformation parameters. (C) 1999 Elsevier Science S.A. All rights reserved.
引用
收藏
页码:244 / 250
页数:7
相关论文
共 24 条
[1]   MODELING MICROSTRUCTURE AND ITS EFFECTS DURING MULTIPASS HOT-ROLLING [J].
BEYNON, JH ;
SELLARS, CM .
ISIJ INTERNATIONAL, 1992, 32 (03) :359-367
[2]  
BOYKO C, 1991, SUPERALLOYS 718 625, P107
[3]   THE THERMAL AND METALLURGICAL STATE OF STEEL STRIP DURING HOT-ROLLING .3. MICROSTRUCTURAL EVOLUTION [J].
DEVADAS, C ;
SAMARASEKERA, IV ;
HAWBOLT, EB .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (02) :335-349
[4]  
DOMBLESKY JP, 1994, SUPERALLOYS 718, 625, 706 AND VARIOUS DERIVATIVES, P263
[5]  
GARCIA CI, 1994, SUPERALLOYS 718, 625, 706 AND VARIOUS DERIVATIVES, P293
[6]  
GARCIA CI, 1992, SUPERALLOYS 1992, P527
[7]  
GARCIA CI, 1991, SUPERALLOYS 718 625, P925
[8]  
GARLSON RG, 1989, SUPERALLOY 718 METAL, P79
[9]   A NEW RELATIONSHIP BETWEEN THE FLOW-STRESS AND THE MICROSTRUCTURAL PARAMETERS FOR DUAL PHASE STEEL [J].
JIANG, ZG ;
LIU, JK ;
LIAN, JH .
ACTA METALLURGICA ET MATERIALIA, 1992, 40 (07) :1587-1597
[10]   RECRYSTALLIZATION OF AUSTENITE AFTER DEFORMATION AT HIGH-TEMPERATURES AND STRAIN RATES - ANALYSIS AND MODELING [J].
LAASRAOUI, A ;
JONAS, JJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (01) :151-160