Development of tungsten-based materials by different sintering techniques

被引：17

作者：

Arshad, Kameel ^{[1
]}

Wang, Jun ^{[1
]}

Yuan, Yue ^{[1
]}

Zhang, Ying ^{[1
]}

Zhou, Zhang-Jian ^{[2
]}

Lu, Guang-Hong ^{[1
]}

机构：

[1] Beihang Univ, Sch Phys & Nucl Energy Engn, Beijing 100191, Peoples R China

[2] Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Beijing 100083, Peoples R China

来源：

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS | 2015年 / 50卷

关键词：

Tungsten vanadium composites; Sintering techniques; Microstructures; Mechanical properties; MECHANICAL-PROPERTIES; GRAINED TUNGSTEN; MICROSTRUCTURES; COMPOSITES; DENSIFICATION; BEHAVIOR;

D O I：

10.1016/j.ijrmhm.2015.02.004

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effects of different sintering techniques on the densification, microstructure, and mechanical properties of tungsten-vanadium composites were investigated. The precursor powders were conventionally mixed with a combination of W-5 wt.%V in a blender and then sintered by three different sintering techniques. A good dense sample with the lowest porosity, and the highest bending strength and micro-hardness was obtained by hot-press sintering, reached up to 3.5%, 508.9 MPa and 589.8 HV0.2, respectively. Spark plasma sintering was beneficial to obtain more refined tungsten grains as compared to hot-press sintering and conventional sintering under hydrogen atmosphere. However, the insufficient sintering conditions of spark plasma sintering were not able to highly suppress the porosity, and thus the mechanical properties were inadequate in comparison with hot press sintering. The properties measured for hydrogen furnace sintered sample were very poor in all respects. (C) 2015 Elsevier Ltd. All rights reserved.

引用

页码：253 / 257

页数：5

共 24 条

[1] Spark-plasma-sintering (SPS) of nanostructured titanium carbonitride powders [J].

Angerer, P ;

Yu, LG ;

Khor, KA ;

Korb, G ;

Zalite, I .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2005, 25 (11) :1919-1927

[2] Influence of vanadium precursor powder size on microstructures and properties of W-V alloy [J].

Arshad, Kameel ;

Guo, Wei ;

Wang, Jun ;

Zhao, Ming-Yue ;

Yuan, Yue ;

Zhang, Ying ;

Wang, Bo ;

Zhou, Zhang-Jian ;

Lu, Guang-Hong .

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2015, 50 :59-64

[3] Effects of vanadium concentration on the densification, microstructures and mechanical properties of tungsten vanadium alloys [J].

Arshad, Kameel ;

Zhao, Ming-Yue ;

Yuan, Yue ;

Zhang, Ying ;

Zhao, Zhen-Hua ;

Wang, Bo ;

Zhou, Zhang-Jian ;

Lu, Guang-Hong .

JOURNAL OF NUCLEAR MATERIALS, 2014, 455 (1-3) :96-100

[4]

Arshad K, 2014, INT BHURBAN C APPL S, P12, DOI 10.1109/IBCAST.2014.6778113

[5] Thermal stability evaluation of microstructures and mechanical properties of tungsten vanadium alloys [J].

Arshad, Kameel ;

Zhao, Ming-Yue ;

Yuan, Yue ;

Zhang, Ying ;

Zhou, Zhang-Jian ;

Lu, Guang-Hong .

MODERN PHYSICS LETTERS B, 2014, 28 (26)

[6] SINTERING ATMOSPHERE EFFECTS ON TENSILE PROPERTIES OF HEAVY ALLOYS [J].

BOSE, A ;

GERMAN, RM .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1988, 19 (10) :2467-2476

[7] Densification and properties of zirconia prepared by three different sintering techniques [J].

Dahl, P. ;

Kaus, I. ;

Zhao, Z. ;

Johnsson, M. ;

Nygren, M. ;

Wiik, K. ;

Grande, T. ;

Einarsrud, M.-A. .

CERAMICS INTERNATIONAL, 2007, 33 (08) :1603-1610

[8]

Frantsevich I. N., 1980, Soviet Powder Metallurgy and Metal Ceramics, V19, P545

[9]

Gilbert M R, 2004, Handbook of activation data calculated using EASY-2003

[10] First-principles investigation on vacancy trapping behaviors of hydrogen in vanadium [J].

Gui, Li-Jiang ;

Liu, Yue-Lin ;

Wang, Wei-Tian ;

Jin, Shuo ;

Zhang, Ying ;

Lu, Guang-Hong ;

Yao, Jun-En .

JOURNAL OF NUCLEAR MATERIALS, 2013, 442 (1-3) :S688-S693

← 1 2 3 →