Effect of stabilised ZrO2, Al2O3 and TiO2 on sintering of hydroxyapatite

被引:15
|
作者
Mezahi, F [1 ]
Harabi, A
Zouai, S
Achour, S
Bernache-Assollant, D
机构
[1] Mohamed Boudiaf Univ, Phys Lab, Msil 28000, Algeria
[2] Mentouri Univ, Ceram Lab, Constantine 25000, Algeria
[3] SPCTS, UMR 6638, Fac Sci, Limoges, France
来源
FUNCTIONALLY GRADED MATERIALS VIII | 2005年 / 492-493卷
关键词
hydroxyapatite; sintering; additions; bone; tricalcium phosphate; resorbtion;
D O I
10.4028/www.scientific.net/MSF.492-493.241
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In this work, the hydroxyapatite was prepared from cortical bone after calcination at 700 C during 1 hour. In order to improve mechanical properties of HA, 5 wt% of the ZrO2 (stabilized with 12.0 wt% CeO2), Al2O3 and TiO2 were added to HA powder as a reinforcing phase. All the powders were sintered at 1300 degrees C for 2 hours. The XRD was utilized to identify the phases composition. It was found that the initial calcined powder is hydroxyapatite with the following chemical composition Ca-5(PO4)(3)OH. In addition, the phenolphthalein test has put into evidence the existence of free CaO. For powders containing ZrO2, the XRD spectra has showed a little percent of formed beta-tricalcium phosphate ((beta-TCP); the HA was decomposed to ((beta-TCP) and CaO which forms with ZrO2 the calcium zirconate (CaZrO3). Nevertheless, in powders containing TiO2, the XRD spectra showed that a partial decomposition of HA to beta-TCP was occurred with formation of calcium titanium oxide (CaTiO3 However, for powders containing Al2O3, a nearly full decomposition of HA to beta-TCP was occurred, the free Al2O3 was present. Finally, it has been found that HA composites containing a large amount of beta-tricalcium phosphate are resorbale than HA composites containing a small amount of beta-TCP and they were not well densified. The microhardness values of HA-ZrO2 composites were greater than those of HA-Al2O3 and HA-TiO2 composites.
引用
收藏
页码:241 / 246
页数:6
相关论文
共 50 条
  • [41] Sintering of α-Al2O3-seeded nanocrystalline γ-Al2O3 powders
    Nordahl, CS
    Messing, GL
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (04) : 415 - 422
  • [42] Sintering kinetics of α-Al2O3 powder
    Zeng, WM
    Gao, L
    Gui, LH
    Guo, JK
    CERAMICS INTERNATIONAL, 1999, 25 (08) : 723 - 726
  • [43] Effect of Nb2O5 addition on Al2O3 - Y2O3 sintering
    Cabral, R. F.
    Louro, L. H. L.
    Campos, J. B.
    Lima, E. S.
    MATERIA-RIO DE JANEIRO, 2014, 19 (02): : 125 - 131
  • [44] Sintering Li2O-Al2O3-4SiO2 precursor powders with ultrafine TiO2 additives
    Wang, MC
    Yang, S
    Wen, SB
    Wu, NC
    MATERIALS CHEMISTRY AND PHYSICS, 2002, 76 (02) : 162 - 170
  • [45] Tailoring the microstructure of mechanoactivated Al2O3 and SiO2 mixtures with TiO2 addition
    Zhang, T. S.
    Kong, L. B.
    Du, Z. H.
    Ma, J.
    Li, S.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 506 (02) : 777 - 783
  • [46] Sintering of α-Al2O3 nanocrystalline ceramic from large α-Al2O3 polycrystalline nanoparticles
    Cao, Wenbin
    Mao, Xuan
    Li, Lu
    Wang, Bing
    Guo, Qian
    Li, Jiangong
    CERAMICS INTERNATIONAL, 2017, 43 (01) : 1378 - 1382
  • [47] PREPARATION AND PROPERTIES OF ZRO2 DISPERSED MGO-AL2O3 CERAMICS .2. EFFECTS OF ZRO2 CONTENT
    FUJITA, M
    YOSHIMATSU, H
    OSAKA, A
    MIURA, Y
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1995, 103 (08) : 838 - 843
  • [48] EFFECT OF SINTERING ON THE CATALYTIC FUNCTIONALITIES OF MOS2 AL2O3 CATALYSTS
    DHAR, GM
    RAMAKRISHNA, H
    RAO, TSRP
    CATALYSIS LETTERS, 1993, 22 (04) : 351 - 359
  • [49] Engineering the toughness of CeO2-stabilised ZrO2
    Vleugels, J
    Van der Biest, O
    EURO CERAMICS VII, PT 1-3, 2002, 206-2 : 273 - 276
  • [50] Study of laser created ZRO2 and hydroxyapatite/ZrO2 films for implantology
    Jelinek, A.
    Dostalova, T.
    Teuberova, Z.
    Seydlova, A.
    Masinova, P.
    Kocourek, T.
    Mroz, W.
    Prokopiuk, A.
    Smetana, K.
    BIOMOLECULAR ENGINEERING, 2007, 24 (01): : 103 - 106