Microstructure and fracture characteristics of spot-welded DP600 steel

被引：178

作者：

Ma, C. ^{[1
]}

Chen, D. L. ^{[1
]}

Bhole, S. D. ^{[1
]}

Boudreau, G. ^{[2
]}

Lee, A. ^{[2
]}

Biro, E. ^{[2
]}

机构：

[1] Ryerson Univ, Dept Mech & Ind Engn, Toronto, ON M5B 2K3, Canada

[2] Dofasco Ltd, Hamilton, ON L8N 3J5, Canada

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2008年 / 485卷 / 1-2期

基金：

加拿大自然科学与工程研究理事会; 加拿大创新基金会;

关键词：

resistance spot welding; expulsion; microstructure; mechanical properties; fatigue; fracture mode; dual-phase steel;

D O I：

10.1016/j.msea.2007.08.010

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Microstructural characterization, microhardness tests, tensile shear tests, and fatigue tests of spot-welded hot dipped galvanized (HDG) DP600 steel were conducted. The effects of weld expulsion on the microstructural characteristics, mechanical properties, and fracture modes were investigated using optical microscopy, image analysis and scanning electron microscopy (SEM) together with energy dispersive X-ray spectroscopy (EDS). The hardness in the weld nugget was observed to be over two times higher than that in the base metal due to the formation of lath martensite. Fatigue tests showed a slightly lower fatigue limit for the joints with the expulsion. The crack initiation was observed to occur basically at the boundary of the weld nugget and at the interface between two sheets. The causes for the interfacial fracture (IF) were discussed in relation to the microstructure and weld parameters. (C) 2007 Elsevier B.V. All rights reserved.

引用

页码：334 / 346

页数：13

共 33 条

[1]

*A SP, 2002, TEST PROC FAT TEST S

[2]

[Anonymous], 2004, INT J JOIN MAT

[3]

CAHOON JR, 1971, METALL TRANS, V2, P1979

[4]

CALLISTER WD, 2007, MAT SCI ENG INTRO, P155

[5]

Chao YJ, 2003, SCI TECHNOL WELD JOI, V8, P133, DOI 10.1179/136217103225008955

[6]

Chien CS, 2002, WELD J, V81, p195S

[7] THE MEASUREMENT OF FATIGUE CRACKS AT SPOT-WELDS [J].

COOPER, JF ;

SMITH, RA .

INTERNATIONAL JOURNAL OF FATIGUE, 1985, 7 (03) :137-140

[8]

EASTERLING K, 1992, INTRO PHYS METALLURG, P76

[9] INFLUENCE OF PRESTRAINING AND AGING ON FATIGUE PROPERTIES OF HIGH-STRENGTH SHEET STEELS [J].

FREDRIKSSON, K ;

MELANDER, A ;

HEDMAN, M .

INTERNATIONAL JOURNAL OF FATIGUE, 1988, 10 (03) :139-151

[10]

Gould JE, 2006, WELD J, V85, p111S

← 1 2 3 4 →