Investigation of positive electrodes after cycle testing of high-power Li-ion battery cells II - An approach to the power fading mechanism using hard X-ray photoemission spectroscopy

被引：59

作者：

Shikano, A. ^{[1
]}

Kobayashi, H. ^{[1
]}

Koike, S. ^{[1
]}

Sakaebe, H. ^{[1
]}

Ikenaga, E. ^{[2
]}

Kobayashi, K. ^{[2
]}

Tatsumi, K. ^{[1
]}

机构：

[1] Natl Inst Adv Ind Sci & Technol, Osaka 638577, Japan

[2] Japan Synchrotron Radiat Res Inst, JASRI, Sayo, Hyogo 6795198, Japan

来源：

JOURNAL OF POWER SOURCES | 2007年 / 174卷 / 02期

关键词：

Li-ion battery; positive electrode; hard X-ray photoemission spectroscopy; X-ray photoemission spectroscopy;

D O I：

10.1016/j.jpowsour.2007.06.138

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

X-ray photoemission spectroscopic and high-resolution hard X-ray photoemission spectroscopic studies of positive electrodes in LiNi(0.73)Co(0.17)Al(0.10)O(2) and hard carbon based batteries were carried out to elucidate the mechanism of battery degradation. Li(2)CO(3), hydrocarbons, ROCO(2)Li, polycarbonate-type compounds and LiF were observed on positive electrode surfaces and the amount of carbonates was found to have increased after cycle testing. Above 60 degrees C, signs of electrolyte decomposition were indicated. Near the surface of the positive electrodes, a Li-deficient cubic phase is present and grows with degradation. Capacity and power fade could be related to the amount of species on the surface and the thickness of the Li-deficient cubic phase near the surface. (C) 2007 Elsevier B.V. All rights reserved.