Study on the Preparation and Lipophilic Properties of Polyvinyl Alcohol (PVA) Nanofiber Membranes via Green Electrospinning

As an environmentally friendly water-soluble polymer, polyvinyl alcohol (PVA) has attracted extensive attention because of its non-toxic, degradable, low cost, and good biocompatibility. Electrospinning is a kind of nanotechnology, and the nanofiber membrane prepared by it has the advantages of large surface area-to-volume ratios, nano- to micron-sized fibers, etc. Herein, a simple and facile one-step green electrospinning method was developed to fabricate various environmentally friendly PVA nanofiber membranes. The lipophilic properties of PVA membranes were investigated and optimized according different PVA concentrations. The PVA electrospun fiber prepared from the solution at a concentration of 10 wt% had the highest adsorption capacity for the adsorption of new and waste engine oils, and the waste engine oil adsorption capacity (12.70 g/g) was higher than that of new engine oil (11.67 g/g). It also has a relatively large BET surface area (12.05 m(2)/g), a pore volume (0.04 cm(3)/g), and an appropriate pore diameter (13.69 nm) and fiber diameter (174.21 nm). All electrospun PVA membranes showed excellent lipophilic properties due to their oil contact angles of much less than 30 degrees. Therefore, PVA electrospun fibrous membranes have great application potential in the field of purifying engine oil due to the excellent lipophilic properties and oil absorption capacity.