Thermomechanical characterization of pure polycrystalline tantalum

被引:49
作者
Rittel, D. [1 ]
Bhattacharyya, A.
Poon, B.
Zhao, J.
Ravichandran, G.
机构
[1] Technion Israel Inst Technol, Fac Mech Engn, IL-32000 Haifa, Israel
[2] CALTECH, Grad Aeronaut Labs, Pasadena, CA 91125 USA
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2007年 / 447卷 / 1-2期
关键词
tantalum; high strain rate; thermomechanics; beta factor; temperature;
D O I
10.1016/j.msea.2006.10.064
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The thermomechanical behavior of pure polycrystalline tantalum has been characterized over a wide range of strain rates, using the recently developed shear compression specimen [D. RitteI, S. Lee, G. Ravichandran, Experimental Mechanics 42 (2002) 58-64]. Dynamic experiments were carried out using a split Hopkinson pressure bar, and the specimen's temperature was monitored throughout the tests using an infrared radiometer. The results of the mechanical tests confirm previous results on pure Ta. Specifically, in addition to its significant strain rate sensitivity, it was observed that pure Ta exhibits very little strain hardening at high strain rates. The measured temperature rise in the specimen's gauge was compared to theoretical predictions which assume a total conversion of the mechanical energy into heat (beta = 1) [G.l. Taylor, H. Quinney, Proceedings of the Royal Society of London, vol. A, 1934, pp. 307-3261, and an excellent agreement was obtained. This result confirms the previous result of Kapoor and Nemat-Nasser [R. Kapoor, S. Nemat-Nasser, Mech. Mater. 27 (1998) 1-12], while a different experimental approach was adopted here. The assumption that = I is found to be justified in this specific case by the lack of dynamic strain hardening of pure Ta. However, this assumption should be limited to non-hardening materials, to reflect the fact that strain hardening implies that part of the mechanical energy is stored into the material's microstructure. (c) 2006 Published by Elsevier B.V.
引用
收藏
页码:65 / 70
页数:6
相关论文
共 26 条
[1]  
BEVER MB, 1973, PROG MATER SCI, V17, P5, DOI [10.1016/0079-6425(73)90001-7, DOI 10.1016/0079-6425(73)90001-7]
[2]  
Boley B.A., 1960, Theory of Thermal Stresses
[3]   Numerical validation of the shear compression specimen. Part II: Dynamic large strain testing [J].
Dorogoy, A. ;
Rittel, D. .
Experimental Mechanics, 2005, 45 (02) :178-185
[4]   Numerical validation of the shear compression specimen. Part 1: Quasi-static large strain testing [J].
Dorogoy, A ;
Rittel, D .
EXPERIMENTAL MECHANICS, 2005, 45 (02) :167-177
[5]  
DOROGOY A, 2005, COMMUNICATION
[6]  
DUPREY KE, 1988, AIP C P, V429, P475
[7]   The heat developed during plastic extension of metals [J].
Farren, WS ;
Taylor, GI .
PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-CONTAINING PAPERS OF A MATHEMATICAL AND PHYSICAL CHARACTER, 1925, 107 (743) :422-451
[8]   MEASUREMENT OF THE TEMPERATURE PROFILE DURING SHEAR BAND FORMATION IN STEELS DEFORMING AT HIGH-STRAIN RATES [J].
HARTLEY, KA ;
DUFFY, J ;
HAWLEY, RH .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1987, 35 (03) :283-301
[9]   TEMPERATURE AND STRAIN RATE DEPENDENCE OF FLOW-STRESS OF TANTALUM [J].
HOGE, KG ;
MUKHERJEE, AK .
JOURNAL OF MATERIALS SCIENCE, 1977, 12 (08) :1666-1672
[10]   Determination of temperature rise during high strain rate deformation [J].
Kapoor, R ;
Nemat-Nasser, S .
MECHANICS OF MATERIALS, 1998, 27 (01) :1-12