Fatigue crack initiation and propagation behavior of Inconel Alloy 690TT steam generator tube

被引：9
作者：
Li, Z. H. [1 ]
Wang, X. Y. [1 ]
Hong, C. [1 ]
Lu, Y. H. [1 ]
Shoji, T. [1 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2021年 / 811卷
关键词：
Alloy; 690TT; Fatigue crack initiation; XFEM; EBSD; Steam generator tube; WATER; MICROSTRUCTURE; EBSD;
D O I：
10.1016/j.msea.2021.141090
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Fatigue crack initiation and propagation behavior of Inconel Alloy 690TT steam generator (SG) tube under 0.2% strain amplitude were studied by scanning electron microscopy (SEM), electron back-scatter diffraction (EBSD) detector and extended finite element method (XFEM). The results showed that the main crack initiated at the discontinuous interface between the persistent slip bands (PSBs) and the matrix in the grain at the edge of the intrados surface. The metastable crack firstly transgranularly transited to the lateral surface, then penetrated steadily along the direction of maximum shear stress, and finally rapidly propagated perpendicularly to the loading axis, which was consistent with the numerical simulation results. Different fracture modes of specimen shape led to different fatigue lives. The fatigue life of tubular specimen was lower than that of bar specimen, the fatigue life of boat-shaped Alloy 690TT SG tube at 0.2% strain amplitude was 11,476 cycles.
引用
收藏
页数：10
相关论文
共 23 条
[1]   Fatigue crack propagation in complex stress fields: Experiments and numerical simulations using the Extended Finite Element Method (XFEM) [J].
Bergara, A. ;
Dorado, J. I. ;
Martin-Meizoso, A. ;
Martinez-Esnaola, J. M. .
INTERNATIONAL JOURNAL OF FATIGUE, 2017, 103 :112-121
[2]   The corrosion behaviour of alloy 690 tube in simulated PWR secondary water with the effect of solid diffusing hydrogen [J].
Chen, Junjie ;
Lu, Zhanpeng ;
Meng, Fanjiang ;
Xu, Xuelian ;
Xiao, Qian ;
Kim, Ho-Sub ;
Jang, Changheui .
JOURNAL OF NUCLEAR MATERIALS, 2019, 517 :179-191
[3]   Comparison of oxide layers formed on the low-cycle fatigue crack surfaces of Alloy 690 and 316 SS tested in a simulated PWR environment [J].
Chen, Junjie ;
Nurrochman, Andrieanto ;
Hong, Jong-Dae ;
Kim, Tae Soon ;
Jang, Changheui ;
Yi, Yongsun .
NUCLEAR ENGINEERING AND TECHNOLOGY, 2019, 51 (02) :479-489
[4]   Low Cycle Fatigue Behavior of Steam Generator Tubes under Axial Loading [J].
He, Xing ;
Chen, Junfeng ;
Tian, Wei ;
Li, Yuebing ;
Jin, Weiya .
MATERIALS, 2018, 11 (10)
[5]   Low cycle fatigue behavior of alloy 690 in simulated PWR water-Effects of dynamic strain aging and hydrogen [J].
Hong, Jong-Dae ;
Lee, Junho ;
Jang, Changheui ;
Kim, Tae Soon .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 611 :37-44
[6]   Effect of mono-tension and biaxial tension on microstructure and stress corrosion cracking of Alloy 690TT [J].
Hou, J. ;
Wang, J. Q. ;
Ke, W. ;
Han, E. H. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 518 (1-2) :19-26
[7]   The heterogeneity of persistent slip band nucleation and evolution in metals at the micrometer scale [J].
Lavenstein, Steven ;
Gu, Yejun ;
Madisetti, Dylan ;
El-Awady, Jaafar A. .
SCIENCE, 2020, 370 (6513) :190-+
[8]   High cycle fatigue behavior and numerical evaluation of Alloy 690TT steam generator tube [J].
Li, Zhenhua ;
Wang, Xinyu ;
Wang, Junping ;
Lu, Yonghao ;
Shoji, Tetsuo .
INTERNATIONAL JOURNAL OF FATIGUE, 2020, 137
[9]   Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 °C pure water [J].
Liao, Jiapeng ;
Tan, Jibo ;
Wu, Xinqiang ;
Tang, Lichen ;
Qian, Hao ;
Xie, Yongcheng .
CORROSION SCIENCE, 2018, 141 :158-167
[10]   Repassivation behavior of alloy 690TT in simulated primary water at different temperatures [J].
Liu, Ji ;
Wang, Jianqiu ;
Zhang, Zhiming ;
Zheng, Hui .
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2021, 68 :227-235
123