Interfacial reaction of alumina ceramics to mild steel braze Joint

被引：1
|
作者：
Li, Zhuoran [1 ]
Wu, Guangdong [1 ]
Zhang, Xianglong [1 ]
Fan, Jianxin [1 ]
Feng, Jicai [1 ]
机构：
[1] Harbin Inst Technol, State Key Lab Adv Welding & Joinging, Harbin 150001, Peoples R China
来源：
MATERIALS PROCESSING TECHNOLOGY, PTS 1-4 | 2011年 / 291-294卷
关键词：
Interfacial reaction; Ceramic brazing; Ag-Cu-Ti filler alloy; Mild Steel; MICROSTRUCTURAL CHARACTERIZATION; TI;
D O I：
10.4028/www.scientific.net/AMR.291-294.954
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Al2O3 is brazed with mild steel using 70Ag-27Cu-3Ti (wt.%) active filler alloy at 900 degrees C for 5 min. The interfacial reaction products are analyzed with X-ray diffraction (XRD). The interfacial phases are analyzed with EDAX. According to the experimental observations, the interfaces developed during brazing have been systematically characterized and the structure are separately Ti3Cu3O/Ti3Al+ TiMn+TiFe2 +Ag(s,s)+Cu(s,s)/TiC from alumina ceramics side to mild steel side.
引用
收藏
页码：954 / 957
页数：4
相关论文
共 50 条
  • [1] Mechanical properties of brazing joint of alumina ceramics to mild steel
    Li, Zhuoran
    Fan, Jianxin
    Feng, Jicai
    Hanjie Xuebao/Transactions of the China Welding Institution, 2009, 30 (10): : 65 - 67
  • [2] A Research on Interfacial Reaction of Brazing Joint of Alumina Ceramics to Metals
    Ma, Xiangdong
    Wang, Xinyang
    Li, Jiwen
    Wei, Shizhong
    PRICM 7, PTS 1-3, 2010, 654-656 : 2732 - +
  • [3] Effect of interfacial thickness and residual stress on the mechanical property of the alumina-stainless steel braze joint interface
    Kar, Abhijit
    Ghosh, Mainak
    Ray, Ashok Kumar
    Ray, Ajoy Kumar
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 498 (1-2): : 283 - 288
  • [4] MICROSTRUCTURAL CHARACTERIZATION OF INTERFACIAL REACTION-PRODUCTS BETWEEN ALUMINA AND BRAZE ALLOY
    LEE, WC
    KWON, OY
    KANG, CS
    JOURNAL OF MATERIALS SCIENCE, 1995, 30 (07) : 1679 - 1688
  • [5] Interfacial reactions in alumina/CuAgTi braze/CuNi system
    Valette, C
    Devismes, MF
    Voytovych, R
    Eustathopoulos, N
    SCRIPTA MATERIALIA, 2005, 52 (01) : 1 - 6
  • [6] On the Joint Formation and Interfacial Microstructure of Cold Metal Transfer Cycle Step Braze Welding of Aluminum to Steel Butt Joint
    Chen, James
    Shalchi Amirkhiz, Babak
    Zhang, Ruby
    Rona, Brian
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2020, 51 (10): : 5198 - 5212
  • [7] On the Joint Formation and Interfacial Microstructure of Cold Metal Transfer Cycle Step Braze Welding of Aluminum to Steel Butt Joint
    James Chen
    Babak Shalchi Amirkhiz
    Ruby Zhang
    Brian Rona
    Metallurgical and Materials Transactions A, 2020, 51 : 5198 - 5212
  • [8] REACTION LAYER CHARACTERIZATION OF THE BRAZE JOINT OF SILICON-NITRIDE TO STAINLESS-STEEL
    XU, R
    INDACOCHEA, JE
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 1994, 3 (05) : 596 - 605
  • [9] Interfacial properties of metallized alumina ceramics
    Sumana Ghosh
    Kalyan Sundar Pal
    Nandadulal Dandapat
    Someswar Datta
    Debabrata Basu
    Metals and Materials International, 2012, 18 : 625 - 630
  • [10] Interfacial properties of metallized alumina ceramics
    Ghosh, Sumana
    Pal, Kalyan Sundar
    Dandapat, Nandadulal
    Datta, Someswar
    Basu, Debabrata
    METALS AND MATERIALS INTERNATIONAL, 2012, 18 (04) : 625 - 630
12345