Synthesis and characterization of a titanium phosphate-tellurite glass for Faraday rotators

This work is focused on investigation of thermal, structural, optical, magnetic, and magneto-optical properties of novel titanium phosphate-tellurite glass applied as Faraday rotators. The glass belonging to the system 35Li(2)O-10Al(2)O(3)-5TiO(2)-45P(2)O(5)-5TeO(2) was prepared by a nonconventional wet route of raw materials processing, followed by melting-quenching-annealing steps. Some important physical properties of the investigated glass have been measured and calculated, providing knowledge related to glass compactness, electronic structure, glass forming capability, etc. XRD analysis evidenced an amorphous network structure of the investigated glass. The optical absorption in the Vis domain is mainly due to Ti3+ ions and Te-2 clusters formed during the glass melting process. A relatively low optical absorption is noticed over 600 nm that activates a significant Faraday magneto-optical effect. Photoluminescence bands in the blue, red, and infrared domains are observed, caused by Te-2 clusters formed during the glass melting process. The magnetization in dependency on applied magnetic field reveals a complex behavior of the glass, depending on temperature. Thus, it is found a ferromagnetic behavior up to 2000 Oe, a paramagnetic component up to 40 000 Oe, followed by a diamagnetic one over 40 000 Oe. Faraday rotation angle and Verdet constant values in the visible domain are correlated with the reduced TeO2 content of the glass.