Electrical resistivity of nanostructured aluminum at low temperature

被引:2
作者
Sun Li-Jun [1 ,2 ]
Dai Fei [2 ]
Luo Jiang-Shan [2 ]
Yi Yong [1 ]
Yang Meng-Sheng [2 ]
Zhang Ji-Cheng [2 ]
Li Jun [2 ]
Lei Hai-Le [2 ]
机构
[1] Southwest Univ Sci & Technol, Sch Mat Sci & Engn, Mianyang 621010, Peoples R China
[2] China Acad Engn Phys, Res Ctr Laser Fus, Mianyang 621900, Peoples R China
关键词
nanostructured aluminum; electrical resistivity; phonon-electron scattering; grain boundary; GRAIN-BOUNDARIES; VIBRATIONAL PROPERTIES; MATTHIESSENS-RULE; FILMS; COPPER;
D O I
10.7498/aps.65.137303
中图分类号
O4 [物理学];
学科分类号
0702 ;
摘要
The nanostructured materials have been revealed to have exclusive physical and chemical properties due to their quantum-size effects, small-size effects and a large fraction of grain boundaries. Especially, the grain boundaries play an important role in the electrical resistivity of nanostructured metal. We use the four-point probe method to measure the values of electrical resistivity (rho) of the nanostructured aluminum samples and the coarse-grained bulk aluminum samples at temperature (T) ranging from 8 K to 300 K to explore the relationship between the electrical resistivity and temperature. The aluminum nanoparticles produced by the flow-levitation method through electromagnetic induction heating are compacted into nanostructured samples in vacuum by the hot pressing and sintering technology. The microstructures of all nanostructured aluminum samples are analyzed by X-ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscope with the energy-dispersive spectrometer (SEM-EDS). The densities of all nanostructured aluminum samples are measured by using the Archimedes method (the medium is absolute alcohol). The experimental results show that the shape of aluminum nanoparticles is found to keep spherical from the SEM images and the relative density of all nanostructured aluminum samples is about 93% of the coarse-grained bulk aluminum. The XRD spectra state that the face-centered cubic (FCC) phase dominates the samples and no diffraction peak related to impurities appears in the XRD spectrum for each of all nanostructured aluminum samples. Amorphous alumina layers (about 2 nm thick) are found to surround the aluminum nanoparticles and hence connect the grains in the nanostructured aluminum as shown in the high-resolution TEM images. Owing to the scattering of grain boundaries on electrons and the phonon-electron scattering at grain boundaries, the electrical resistivity is far larger in the nanostructured aluminum than in the coarse-grained bulk aluminum and the relationship between the electrical resistivity and temperature for nanostructured aluminum shows a different feature from that for the coarse-grained bulk aluminum. Although the temperature dependent electrical resistivity (rho(T)) is a function of T-4 at low temperatures for the coarse-grained bulk aluminum, it varies with the temperature not only according to the relation T-4, but also according to the relation T-3 for the nanostructured aluminum. The residual resistivity (rho(0)) of the nanostructured aluminum sample is about 5.5 x 10(-4) Omega.m, 5-6 orders magnitude larger than that of the coarse-grained bulk aluminum (2.01 x 10(-10) Omega.m) due to the scattering of both the grain boundaries and amorphous alumina on electrons therein.
引用
收藏
页数:6
相关论文
共 32 条
[21]   Experiment study of the size effects on electron-phonon relaxation and electrical resistivity of polycrystalline thin gold films [J].
Ma, W. G. ;
Wang, H. D. ;
Zhang, X. ;
Wang, W. .
JOURNAL OF APPLIED PHYSICS, 2010, 108 (06)
[22]   ELECTRICAL-RESISTIVITY MODEL FOR POLYCRYSTALLINE FILMS - CASE OF ARBITRARY REFLECTION AT EXTERNAL SURFACES [J].
MAYADAS, AF ;
SHATZKES, M .
PHYSICAL REVIEW B, 1970, 1 (04) :1382-&
[23]   TEMPERATURE-DEPENDENCE OF ELECTRICAL-RESISTIVITY OF COPPER AT LOW-TEMPERATURES [J].
MOUSSOUROS, PK ;
KOS, JF .
CANADIAN JOURNAL OF PHYSICS, 1977, 55 (23) :2071-2079
[24]   Anomalous electrical transport behavior in nanocrystalline nickel [J].
Okram, G. S. ;
Soni, Ajay ;
Rawat, R. .
NANOTECHNOLOGY, 2008, 19 (18)
[25]   Thermal stability of nanocrystalline gold prepared by gas deposition method [J].
Okuda, S ;
Tang, F .
NANOSTRUCTURED MATERIALS, 1995, 6 (5-8) :585-588
[26]   Electrical resistivity of fully-relaxed grain boundaries in nanocrystalline Cu [J].
Qian, LH ;
Lu, QH ;
Kong, WJ ;
Lu, K .
SCRIPTA MATERIALIA, 2004, 50 (11) :1407-1411
[27]   Electrical properties of copper films produced by MOCVD [J].
Riedel, S ;
Rober, J ;
Gessner, T .
MICROELECTRONIC ENGINEERING, 1997, 33 (1-4) :165-172
[28]  
[宋言红 Song Yanhong], 2015, [原子能科学技术, Atomic Energy Science and Technology], V49, P354
[29]   ELECTRON PHONON ENERGY EXCHANGE AND LOCAL-FIELDS IN ISLAND METALLIC-FILMS [J].
TOMCHUK, PM .
INTERNATIONAL JOURNAL OF ELECTRONICS, 1992, 73 (05) :949-953
[30]  
[韦建军 Wei Jianjun], 2003, [强激光与粒子束, High Power Laser and Particle Beams], V15, P359