Modeling of Biaxial Compression Behavior of Carbon Fiber-Reinforced Composite after Low-Velocity Impact

被引：4
|
作者：
Yang, Bin [1 ]
Fu, Kunkun [1 ]
Li, Yan [1 ]
机构：
[1] Tongji Univ, Sch Aerosp Engn & Appl Mech, Shanghai 200092, Peoples R China
来源：
JOURNAL OF AEROSPACE ENGINEERING | 2022年 / 35卷 / 03期
基金：
中国博士后科学基金;
关键词：
Carbon fiber-reinforced composite (CFRC); Biaxial compression; Compression after impact (CAI) strength; Finite element (FE); GROWTH PHENOMENA; DAMAGE; FAILURE; PANELS; DELAMINATION; SIMULATION; CRITERION; EVOLUTION; LAMINATE; TENSILE;
D O I：
10.1061/(ASCE)AS.1943-5525.0001417
中图分类号：
V [航空、航天];
学科分类号：
08 ; 0825 ;
摘要：
This study presents a finite-element (FE) model considering intralaminar damage and interlaminar delamination to predict the biaxial compression behavior of carbon fiber-reinforced composites (CFRCs) with low-velocity impact damage. First, the FE model was validated by a uniaxial compression experiment. The FE predictions in terms of compression after impact (CAI) strength and failure patterns were consistent with the experimental results. Then the validated FE model was used to predict the biaxial compression behavior of the CFRCs. It was found that the residual strength of the CFRCs was dependent on the buckling mode of the laminate due to the coupling effect of the longitudinal and transverse compressive loadings. Correspondingly, the CAI strength under biaxial compression was lower than that under longitudinal or transverse compressive loading.
引用
收藏
页数：12
相关论文
共 50 条
  • [21] Autonomic healing of low-velocity impact damage in fiber-reinforced composites
    Patel, Amit J.
    Sottos, Nancy R.
    Wetzel, Eric D.
    White, Scott R.
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2010, 41 (03) : 360 - 368
  • [22] Study on the damage behavior of carbon fiber composite after low-velocity impact under hygrothermal aging
    Zhou, Song
    Jia, Yao Xiong
    Xu, Liang
    Wang, Lei
    Hui, Li
    JOURNAL OF APPLIED POLYMER SCIENCE, 2021, 138 (17)
  • [23] Research on carbon fiber-reinforced plastic bumper beam subjected to low-velocity frontal impact
    Hu, Yefa
    Liu, Can
    Zhang, Jinguang
    Ding, Guoping
    Wu, Qiong
    ADVANCES IN MECHANICAL ENGINEERING, 2015, 7 (06): : 1 - 15
  • [24] Effect of nanosilica on low-velocity impact and compression after impact properties of continuous carbon fiber-reinforced epoxy composites manufactured by 3D printing
    Wagmare, Rajkumar
    Harshe, Rahul
    Pednekar, Jaising
    Patro, T. Umasankar
    Joshi, Makarand
    POLYMER COMPOSITES, 2023, 44 (11) : 7794 - 7803
  • [25] Low-Velocity Impact and Compression after Impact Properties of Hemp and Jute Fiber Reinforced Epoxy Composites
    Patil, Shreekant
    Reddy, Dagalahal Mallikarjuna
    Naveen, J.
    Swamy, S. S.
    Vignesh, P.
    Venkatachalam, G.
    JOURNAL OF NATURAL FIBERS, 2022, 19 (15) : 12309 - 12324
  • [26] Low-velocity impact response and compression after impact behavior of tubular composite sandwich structures
    Zhang, Chao
    Tan, K. T.
    COMPOSITES PART B-ENGINEERING, 2020, 193
  • [27] Residual compressive strength of polyamide fiber-reinforced epoxy composites after low-velocity impact
    Coskun, Taner
    Yar, Adem
    Demir, Okan
    Sahin, Omer Sinan
    POLYMER COMPOSITES, 2023, 44 (05) : 2671 - 2684
  • [28] Damage and Failure of Laminated Carbon-Fiber-Reinforced Composite under Low-Velocity Impact
    Wang, Wenzhi
    Wan, Xiaopeng
    Zhou, Jun
    Zhao, Meiying
    Li, Yulong
    Shang, Shen
    Gao, Xiaosheng
    JOURNAL OF AEROSPACE ENGINEERING, 2014, 27 (02) : 308 - 317
  • [29] Damage and failure of laminated carbon-fiber-reinforced composite under low-velocity impact
    Gao, X. (xgao@uakron.edu), 1600, American Society of Civil Engineers (ASCE), United States (27):
  • [30] Low-velocity impact resistance of the Z-pin reinforced carbon fiber composite laminates
    Wu, Wenyun
    Guo, Zhangxin
    Shi, Haolin
    Niu, Weijing
    Chai, Gin Boay
    Li, Yongcun
    POLYMER COMPOSITES, 2025, 46 (02) : 1699 - 1713
12345