The effects of particle characteristics on three-body abrasive wear

被引:140
作者
Stachowiak, GB [1 ]
Stachowiak, GW [1 ]
机构
[1] Univ Western Australia, Tribol Lab, Dept Mech & Mat Engn, Nedlands, WA 6709, Australia
基金
澳大利亚研究理事会;
关键词
three-body abrasion; abrasive particles; particle angularity; spike parameter;
D O I
10.1016/S0043-1648(01)00557-9
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
The effects of abrasive particle characteristics, especially shape and hardness, on three-body abrasive wear of metallic samples have been investigated. The experimental tests were carried out on a modified pin-on-disc tribometer using dry abrasive particles and on a ball-on-plate tribometer using slurry. Spike parameter quadratic fit (SPQ) was used in the characterization of particles angularity. Better correlation between wear rates and particle angularity was found in ball-on-plate tests. The noted exception was quartz that generated less wear in ah the tests than could be expected from its high SPQ value. Additional characteristics such as particle toughness, orientation in the contact, and embedment in the worn surfaces affected the wear results. Damage due to rolling (indentation) wear prevailed on the plate samples from ball-on-plate tests, whereas both sliding and rolling wear was found on the cylindrical samples from modified pin-on-disc tests. The morphology of worn surfaces correlated well with the shapes of abrasive particles. Rounded particles generated round craters and smooth grooves while angular particles produced sharp indents and narrow cutting grooves. (C) 2001 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:201 / 207
页数:7
相关论文
共 27 条
[1]  
*ASM COMM, 1984, MET HDB, V7, P233
[2]   ERODENT PARTICLE CHARACTERIZATION AND THE EFFECT OF PARTICLE-SIZE AND SHAPE ON EROSION [J].
BAHADUR, S ;
BADRUDDIN, R .
WEAR, 1990, 138 (1-2) :189-208
[3]  
*BRIT STAND, 1965, 2955 BRIT STAND
[4]   A MULTISCALE MEASURE OF PARTICLE ABRASIVITY [J].
HAMBLIN, MG ;
STACHOWIAK, GW .
WEAR, 1995, 185 (1-2) :225-233
[5]   A multi-scale measure of particle abrasivity, and its relation to two-body abrasive wear [J].
Hamblin, MG ;
Stachowiak, GW .
WEAR, 1995, 190 (02) :190-196
[6]   THE EFFECT OF HARDNESS ON THE TRANSITION OF THE ABRASIVE WEAR MECHANISM OF STEELS [J].
HOKKIRIGAWA, K ;
KATO, K ;
LI, ZZ .
WEAR, 1988, 123 (02) :241-251
[7]   THE EFFECT OF ERODENT PARTICLE CHARACTERISTICS ON THE EROSION OF METALS [J].
LIEBHARD, M ;
LEVY, A .
WEAR, 1991, 151 (02) :381-390
[8]   MORPHOLOGICAL FOURIER DESCRIPTORS [J].
LUERKENS, DW ;
BEDDOW, JK ;
VETTER, AF .
POWDER TECHNOLOGY, 1982, 31 (02) :209-215
[9]  
MISRA A, 1981, WEAR, V68, P33, DOI 10.1016/0043-1648(81)90017-X
[10]   ON THE SIZE EFFECT IN ABRASIVE AND EROSIVE WEAR [J].
MISRA, A ;
FINNIE, I .
WEAR, 1981, 65 (03) :359-373