Steel activation in concrete following interruption of long-term cathodic polarization

被引：28

作者：

Presuel-Moreno, F ^{[1
]}

Sagüés, AA ^{[1
]}

Kranc, SC ^{[1
]}

机构：

[1] Univ S Florida, Dept Civil & Environm Engn, Tampa, FL 33620 USA

来源：

CORROSION | 2005年 / 61卷 / 05期

关键词：

cathodic prevention; chloride threshold; concrete; polarization; potential; rebar;

D O I：

10.5006/1.3280642

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A set of partially immersed reinforced concrete columns with mature corrosion patterns was used to demonstrate that corrosion macrocell currents provided "cathodic prevention" to parts of the steel assembly that remained passive even though it was exposed to high chloride concentrations (up to similar to 4.7% of the cement weight) by the end of nine years of testing. The potential of that steel increased following macrocell decoupling, and instances of depassivation were observed 15 days to 75 days after decoupling. The results are contrasted with previous observations of potential dependence of the chloride corrosion threshold in concrete, and an approximate functional relationship between the threshold value and the potential is proposed.

引用

页码：428 / 436

页数：9

共 48 条

[1] Chloride threshold dependence of pitting potential of reinforcements [J].

Alonso, C ;

Castellote, M ;

Andrade, C .

ELECTROCHIMICA ACTA, 2002, 47 (21) :3469-3481

[2]

Alonso C, 2000, RILEM PROC, V19, P415

[3]

ALONSO C, 1997, P 10 INT C CHEM CEM, V4

[4] Electrochemical behaviour of steel rebars in concrete:: influence of environmental factors and cement chemistry [J].

Andrade, C ;

Keddam, M ;

Nóvoa, XR ;

Pérez, MC ;

Rangel, CM ;

Takenouti, H .

ELECTROCHIMICA ACTA, 2001, 46 (24-25) :3905-3912

[5]

ANDRADE C, 1994, AM SOC TEST MATER, V1194, P282, DOI 10.1520/STP24889S

[6] On-site measurements of corrosion rate of reinforcements [J].

Andrade, C ;

Alonso, C .

CONSTRUCTION AND BUILDING MATERIALS, 2001, 15 (2-3) :141-145

[7]

[Anonymous], TVBM3081 LUND U DIV

[8]

ARUP H, 1996, DURABILITY CONCRETE, P107

[9] EFFECT OF CEMENT TYPE ON CHLORIDE BINDING AND CORROSION OF STEEL IN CONCRETE [J].

ARYA, C ;

XU, Y .

CEMENT AND CONCRETE RESEARCH, 1995, 25 (04) :893-902

[10]

*ASTM C, 2004, 1152704 ASTM C, P637

← 1 2 3 4 5 →