High frequency induction brazing of TiC cermets to steel with Ag-Cu-Zn foil

被引：11

作者：

Zhang, L. X. ^{[1
]}

Feng, J. C. ^{[1
]}

Liu, H. B. ^{[1
]}

机构：

[1] Harbin Inst Technol, Natl Key Lab Adv Welding Prod Technol, Harbin 150001, Peoples R China

来源：

MATERIALS SCIENCE AND TECHNOLOGY | 2008年 / 24卷 / 05期

关键词：

high frequency induction brazing; microstructure; mechanical properties; cermets; steel;

D O I：

10.1179/174328408X294107

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

High frequency induction brazing of TiC cermets to steel using Ag-54Cu-33Zn (wt-%) foil at 1073-1273 K for 30-300 s was investigated in the present paper. Both interfacial microstructure and mechanical properties of the brazed joints were studied. Microstructural analysis results show that the interface can be divided into three reaction layers and the formation products on the joint are Cu(SS) (where SS means solid solution), Ni3ZnC0.7 and Ag (SS). With increasing brazing parameters, the thickness of Cu (SS)+Ni3ZnC0.7 layers beside base metals increases. The relationship between processing parameters and shear strength of the joints indicates that the highest shear strength value 105 MPa can be achieved when the joint is brazed at 1123 K for 60 s.

引用

页码：623 / 626

页数：4

共 50 条

[41] Interfacial microstructure and mechanical properties of tungsten carbide brazed joints using Ag-Cu-Zn plus Ni/Mn filler alloy [J].

Hasanabadi, Mahyar ;

Shamsipur, Ali ;

Najafi Sani, Hasan ;

Omidvar, Hamid ;

Sakhaei, Sima .

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2017, 27 (12) :2638-2646

[42] Microstructural Study of Al-Ag-Cu-Si Filler Metal for Brazing High-Strength Aluminum Alloys to Stainless Steel [J].

Fedorov, Vasilii ;

Uhlig, Thomas ;

Podlesak, Harry ;

Wagner, Guntram .

METALS, 2020, 10 (12) :1-8

[43] Vacuum brazing of TiAl to 42CrMo steel with Ag-Cu-Ti filler metal [J].

Li, YL ;

Feng, JC ;

He, P .

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2005, 15 :331-334

[44] Wetting and reaction between β′-sialon, stainless steel and Cu-Ag brazing alloys containing Ti [J].

Abed, A ;

Jalham, IS ;

Hendry, A .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2001, 21 (03) :283-290

[45] Brazing of Ti-48Al-2Cr-2Nb and TiC/Ti matrix composite using Ag-28Cu filler alloy [J].

Zhu Dongdong ;

Xu Haitao ;

Dong Duo ;

He Yanming ;

Zhao Xinyu ;

He Qing .

RESULTS IN PHYSICS, 2019, 14

[46] TiC-xNi composite coatings by high-frequency induction-heated combustion synthesis and their corrosion resistance in molten brass [J].

Pan, Chenggang ;

Liu, Can ;

He, Peng ;

Liu, Dudu ;

Li, Shanshan ;

Zhang, Tao ;

Tang, Yaoyang ;

Yang, Yu ;

Zhai, Yuhui .

MATERIALS CHEMISTRY AND PHYSICS, 2025, 343

[47] Laminated Forming of TC4 Titanium Alloy by High Frequency Induction Brazing [J].

Zhang Jing ;

Zhang Tao ;

Cheng Yangyang .

RARE METAL MATERIALS AND ENGINEERING, 2017, 46 (11) :3440-3445

[48] Temperature uniformity of profiled grinding wheel under high-frequency induction brazing [J].

Li Qilin ;

Ding Kai ;

Lei Weining ;

Kong Linglei ;

Chen Jiajia ;

Shan Daping ;

Wang Xichao .

The International Journal of Advanced Manufacturing Technology, 2021, 117 :1091-1099

[49] Iterative Semi-auto-labeling Method for High-Frequency Induction Brazing [J].

Kim, Min-Gwan ;

Moon, Joonhyeok ;

Kang, Ok Hyun ;

Lee, Heejong ;

Oh, Ki-Yong .

INTERNATIONAL JOURNAL OF PRECISION ENGINEERING AND MANUFACTURING-GREEN TECHNOLOGY, 2025, 12 (03) :829-851

[50] Temperature uniformity of profiled grinding wheel under high-frequency induction brazing [J].

Qilin, Li ;

Kai, Ding ;

Weining, Lei ;

Linglei, Kong ;

Jiajia, Chen ;

Daping, Shan ;

Xichao, Wang .

INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2021, 117 (3-4) :1091-1099

← 1 2 3 4 5 →