High frequency induction brazing of TiC cermets to steel with Ag-Cu-Zn foil

被引:11
作者
Zhang, L. X. [1 ]
Feng, J. C. [1 ]
Liu, H. B. [1 ]
机构
[1] Harbin Inst Technol, Natl Key Lab Adv Welding Prod Technol, Harbin 150001, Peoples R China
关键词
high frequency induction brazing; microstructure; mechanical properties; cermets; steel;
D O I
10.1179/174328408X294107
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
High frequency induction brazing of TiC cermets to steel using Ag-54Cu-33Zn (wt-%) foil at 1073-1273 K for 30-300 s was investigated in the present paper. Both interfacial microstructure and mechanical properties of the brazed joints were studied. Microstructural analysis results show that the interface can be divided into three reaction layers and the formation products on the joint are Cu(SS) (where SS means solid solution), Ni3ZnC0.7 and Ag (SS). With increasing brazing parameters, the thickness of Cu (SS)+Ni3ZnC0.7 layers beside base metals increases. The relationship between processing parameters and shear strength of the joints indicates that the highest shear strength value 105 MPa can be achieved when the joint is brazed at 1123 K for 60 s.
引用
收藏
页码:623 / 626
页数:4
相关论文
共 50 条
[31]   Vacuum Brazing of Metallized YSZ and Crofer Alloy Using 72Ag-28Cu Filler Foil [J].
Huang, Liang-Wei ;
Shiue, Ren-Kae ;
Liu, Chien-Kuo ;
Cheng, Yung-Neng ;
Lee, Ruey-Yi ;
Tsay, Leu-Wen .
MATERIALS, 2022, 15 (03)
[32]   Optimized design of composition and brazing process for Cu-Ag-Zn-Mn-Ni-Si-B-P alloy brazing material based on machine learning strategy to improve brazing properties [J].
Fang, Jiheng ;
Xie, Ming ;
Zhang, Jiming ;
Hu, Jieqiong ;
Liu, Guohua ;
Zhao, Shangqiang ;
Chen, Yongtai ;
He, Xingqun ;
Jin, Qinglin .
MATERIALS TODAY COMMUNICATIONS, 2024, 39
[33]   Optimization design of electromagnetism induction heating technical parameters in high frequency induction brazing [J].
Peng, HE ;
Feng, JC ;
Liu, HJ ;
Han, JC ;
Liu, LC .
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2003, 13 :34-38
[34]   Brazing of graphite and stainless steel with Ag-Cu-Ti filler: Effects of brazing process parameters on microstructure and mechanical properties [J].
Deng, Juanli ;
Li, Hao ;
Deng, Mengjia ;
Xia, Xiaoyu ;
Liu, Jiaolong ;
Fan, Shangwu ;
Zhang, Litong ;
Cheng, Laifei .
MATERIALS TODAY COMMUNICATIONS, 2021, 28
[35]   High Frequency Induction Brazing Process of Copper-Steel and Its Effects on Microstructure and Electrical Conductivity of Weld Joint [J].
Shi Y. ;
Gao H. ;
Li G. ;
Li X. .
2018, Cailiao Daobaoshe/ Materials Review (32) :909-914
[36]   Understanding the temperature distribution and influencing factors during high-frequency induction brazing of CBN super-abrasive grains [J].
Xu, Wei ;
Ding, Wenfeng ;
Zhu, Yejun ;
Huang, Xin ;
Fu, Yucan .
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2017, 88 (1-4) :1075-1087
[37]   Nd:YAG pulsed laser brazing of cBN to steel matrix with Zr modified Ag-Cu-Ti active brazing alloy [J].
Huang, Yonggui ;
Liang, Guoxing ;
Lv, Ming ;
Li, Guang ;
Liu, Donggang .
DIAMOND AND RELATED MATERIALS, 2020, 104
[38]   Composite brazing of high thermal mismatched Cf/SiC and 304 stainless steel with foil (Cu)+Ti5Si3 alloy as filler [J].
Wang, Yonglei ;
Zhang, Keke ;
Yin, Danqing .
MATERIALS LETTERS, 2023, 351
[39]   Online welding quality monitoring for large-size electrical contact high frequency induction brazing [J].
Zhu Shiliang ;
Li Qiwei ;
Zhang Zhongdian ;
Tian Xiubo .
MEASUREMENT, 2015, 69 :64-71
[40]   Interfacial characteristics of high frequency induction brazed Cu and pre-metalized graphite joints [J].
Xie Feng-chun ;
Zhang Li-xia ;
He Peng ;
Feng Ji-cai .
JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY, 2009, 16 (06) :902-905