Influence of degree of crystallinity and syndiotacticity on infrared spectra of solid PVA

被引:41
作者
Sugiura, K [1 ]
Hashimoto, M [1 ]
Matsuzawa, S [1 ]
Yamaura, K [1 ]
机构
[1] Shinshu Univ, Fac Text Sci & Technol, Ueda, Nagano 3868567, Japan
关键词
poly(vinyl alcohol); infrared spectroscopy; NMR; syndiotactic; degree of crystallization;
D O I
10.1002/app.1963
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
The influence of the degree of crystallinity and the syndiotacticity on the 1145, 1095, and 916 cm(-1) bands was studied. The intensity of the 1145 cm(-1) band increased with increasing syndiotacticity at a low degree of crystallinity and with an increasing degree of crystallinity for a sample with syndiotacticity. The intensity of 1095 cm(-1) band increased with increasing syndiotacticity at a fixed degree of crystallinity and was independent of the degree of crystallinity for a sample. The intermolecular hydrogen bonds were found to play an important role. The differences of the relations between the absorbance ratio D-1145/D-1095 and the degree of crystallinity with syndiotacticity were explained. The extent of the decrease of the intensity of 916 cm(-1) band with an increasing degree of crystallinity increased with decreasing syndiotacticity. The predominant introduction of syndiotactic sequences in the crystals was assumed in the lower syndiotacticity. The improved equation between the syndiotactic diad content in percent [s-(diad) %] and the absorbance ratio D-916/D-849 was established as s-(diad) % = 71.1 X (D-916/D-849)(0.327) for the films heated at 50 degreesC with use of a syndiotactic. diad content obtained from NMR spectra. (C) 2001 John Wiley & Sons, Inc.
引用
收藏
页码:1291 / 1298
页数:8
相关论文
共 30 条
[1]   LATERALLY ORDERED POLYMERS - POLYACRYLONITRILE AND POLY(VINYL TRIFLUOROACETATE) [J].
BOHN, CR ;
STATTON, WO ;
SCHAEFGEN, JR .
JOURNAL OF POLYMER SCIENCE, 1961, 55 (162) :531-&
[2]   RAMAN SPECTRAL STUDY OF SOLID AND DISSOLVED POLY(VINYL ALCOHOL) AND ETHYLENE-VINYL ALCOHOL COPOLYMER [J].
COONEY, TF ;
WANG, L ;
SHARMA, SK ;
GAULDIE, RW ;
MONTANA, AJ .
JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 1994, 32 (07) :1163-1174
[3]   POLARIZED INFRA-RED RADIATION AS AN AID TO THE STRUCTURAL ANALYSIS OF LONG-CHAIN POLYMERS .1. [J].
ELLIOTT, A ;
AMBROSE, EJ ;
TEMPLE, RB .
JOURNAL OF CHEMICAL PHYSICS, 1948, 16 (09) :877-886
[4]  
FUJII K, 1963, MAKROMOLEKUL CHEM, V65, P74
[5]   POLYVINYL TRIFLUOROACETATE [J].
HAAS, HC ;
EMERSON, ES ;
SCHULER, NW .
JOURNAL OF POLYMER SCIENCE, 1956, 22 (101) :291-302
[6]   CROSS POLARIZATION MAGIC ANGLE SPINNING C-12 NMR-STUDY OF SOLID STRUCTURE AND HYDROGEN-BONDING OF POLY(VINYL ALCOHOL) FILMS WITH DIFFERENT TACTICITIES [J].
HORII, F ;
HU, S ;
ITO, T ;
ODANI, H ;
KITAMARU, R ;
MATSUZAWA, S ;
YAMAURA, K .
POLYMER, 1992, 33 (11) :2299-2306
[7]  
Hu S., 1991, B I CHEM RES KYOTO U, V69, P165
[8]   INFRARED SPECTRA OF HIGH POLYMERS .5. POLYVINYL ALCOHOL [J].
KRIMM, S ;
LIANG, CY ;
SUTHERLAND, GBBM .
JOURNAL OF POLYMER SCIENCE, 1956, 22 (101) :227-247
[9]  
LING CY, 1959, J POLYM SCI, V35, P303
[10]   PHOTOPOLYMERIZATION OF VINYL MONOMERS USING BENZOPHENONE-TETRAHYDROFURAN INITIATION SYSTEM AND ALDEHYDES AT LOW-TEMPERATURES [J].
MATSUZAWA, S ;
YAMAURA, K ;
YAMADA, S ;
SHINKE, Y ;
NAKANO, Y ;
KOIKE, Y .
JOURNAL OF APPLIED POLYMER SCIENCE, 1988, 35 (02) :391-396