Evaluation of High Temperature Oxidation Behaviour of Nanostructured Cr/Co-Al Coatings

被引：9

作者：

Rahman, Atikur ^{[1
]}

Chawla, Vipin ^{[2
]}

Jayaganthan, R. ^{[1
]}

Chandra, Ramesh ^{[2
]}

Ambardar, R. ^{[3
]}

机构：

[1] Indian Inst Technol Roorkee, Dept Met & Mat Engn, Roorkee 247667, Uttar Pradesh, India

[2] Indian Inst Technol Roorkee, Inst Instrumentat Ctr, Roorkee 247667, Uttar Pradesh, India

[3] Natl Inst Technol Hazratbal, Dept Met Engn, Srinagar 190006, Jammu & Kashmir, India

来源：

OXIDATION OF METALS | 2010年 / 74卷 / 5-6期

关键词：

Sputtering; Cr/Co-Al coatings; Microstructures; High temperature oxidation; HOT-CORROSION BEHAVIOR; NI-CR ALLOYS; SELECTIVE OXIDATION; CYCLIC OXIDATION; GRAIN-SIZE; RESISTANCE; SCALE; NANOCRYSTALLIZATION; 900-DEGREES-C; SUPERALLOY;

D O I：

10.1007/s11085-010-9217-3

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The high temperature oxidation behavior of sputtered Cr/Co-Al coatings fabricated by DC/RF magnetron sputtering on a superalloy substrate has been studied in the present work. The microstructural features and phase formation of the as-deposited coatings were characterized by FE-SEM, AFM, and XRD, respectively. Weight-change measurements were made to calculate the cyclic oxidation kinetics of the coated superalloy exposed to air at 900 degrees C. It was observed that the corrosion rate of sputtered Cr/Co-Al coated superalloy is lower than that of the uncoated superalloy owing to the formation of continuous, dense, adherent and protective oxide scales over the surface of the coatings. The protective oxide scales in the corroded coatings were basically the thin layer of Cr2O3, CoO, Al2O3 and CoCr2O4, which provide protection to the base superalloy at high temperature.

引用

页码：341 / 358

页数：18

共 50 条

[1] Evaluation of High Temperature Oxidation Behaviour of Nanostructured Cr/Co–Al Coatings
Atikur Rahman
Vipin Chawla
R. Jayaganthan
Ramesh Chandra
R. Ambardar
Oxidation of Metals, 2010, 74 : 341 - 358
[2] High temperature oxidation behaviour of Cr/Co-Al coated superalloy
Rahman, A.
Chawla, V.
Jayaganthan, R.
Chandra, R.
Tewari, V. K.
Ambardar, R.
SURFACE ENGINEERING, 2012, 28 (04) : 249 - 256
[3] Hot corrosion of nanostructured Cr/Co-Al coatings
Rahman, A.
Chawla, V.
Jayaganthan, R.
Chandra, R.
Ambardar, R.
SURFACE ENGINEERING, 2012, 28 (04) : 285 - 293
[4] Microstructural Characterisations and High Temperature Oxidation Studies of Nanostructured Co-Al Coatings Deposited on Superalloy
Rahman, Atikur
Chawla, Vipin
Jayaganthan, R.
Chandra, Ramesh
Ambardar, R.
Mohamed, S. Beer
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2012, 65 (02) : 205 - 217
[5] High temperature degradation behavior of sputtered nanostructured Co-Al coatings on superalloy
Rahman, Atikur
Jayaganthan, R.
Chandra, Ramesh
Ambardar, R.
APPLIED SURFACE SCIENCE, 2013, 265 : 10 - 23
[6] Study of cyclic hot corrosion of nanostructured Cr/Co-Al coatings on superalloy
Rahman, Atikur
Chawla, Vipin
Jayaganthan, R.
Chandra, Ramesh
Ambardar, R.
MATERIALS CHEMISTRY AND PHYSICS, 2011, 126 (1-2) : 253 - 261
[7] HIGH-TEMPERATURE OXIDATION RESISTANCE OF CO-AL ALLOYS
IRVING, GN
STRINGER, J
WHITTLE, DP
OXIDATION OF METALS, 1975, 9 (05): : 427 - 440
[8] Microstructural Characterization and Cyclic Hot Corrosion Behaviour of Sputtered Co-Al Nanostructured Coatings on Superalloy
Rahman, Atikur
Jayaganthan, R.
Chandra, Ramesh
Ambardar, R.
OXIDATION OF METALS, 2011, 76 (3-4): : 307 - 330
[9] Degradation behaviour of sputtered Co-Al coatings on superalloy
Rahman, Atikur
Chawla, Vipin
Jayaganthan, R.
Chandra, Ramesh
Ambardar, R.
MATERIALS CHEMISTRY AND PHYSICS, 2013, 138 (01) : 49 - 62
[10] Cyclic high temperature oxidation behaviour of sputtered Cr/Al multilayer coatings on superalloy
Rahman, A.
Jayaganthan, R.
Prakash, S.
Chawla, V.
Chandra, R.
SURFACE ENGINEERING, 2011, 27 (05) : 393 - 401

← 1 2 3 4 5 →