Synthesis and optimization of the magnetic properties of aligned strontium ferrite nanowires

被引：8
作者：
Ebrahimi, Fatemeh [1 ]
Bakhshi, Saeed Reza [2 ]
Ashrafizadeh, Fakhreddin [1 ]
Ghasemi, Ali [2 ]
机构：
[1] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran
[2] Malek Ashtar Univ Technol, Dept Mat Engn, Shahin Shahr, Iran
来源：
MATERIALS RESEARCH BULLETIN | 2016年 / 76卷
关键词：
Magnetic materials; Nanostructures; Electron microscopy; Sol-gel chemistry; Magnetic properties;
D O I：
10.1016/j.materresbull.2015.11.061
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
High aspect ratio strontium hexaferrite nanowires were fabricated by dip coating in alumina template. Fe/Sr ratio was changed from 10 to 12 in precursor, and the samples were annealed at a range of temperatures 500-900 degrees C in order to optimize the magnetic properties of strontium ferrite in the form of nanowires. Field emission scanning electron microscope (FESEM) proved the formation of nanowires in the templates, while TEM images revealed a high degree of crystallinity. The ferrites were further characterized by X-ray diffraction (XRD) and energy dispersive X-ray spectrometer (EDS). Magnetic properties of the specimens were studied by a SQUID at 10-300 K. The results showed that the coercivity of packed density nanowires in the template was much less than that of the nanopowders. On the other hand, the coercivity of nanowires at ambient temperature was less than low temperature coercivity. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：240 / 246
页数：7
相关论文
共 50 条
[41]   Controllable Synthesis and Magnetic Properties of Ferromagnetic Nanowires and Nanotubes [J].
Wang, Xue Wei ;
He, Zhao Cheng ;
Li, Ju Shan ;
Yuan, Zhi Hao .
CURRENT NANOSCIENCE, 2012, 8 (05) :801-809
[42]   Facile synthesis and magnetic properties of manganese dioxide nanowires [J].
Du, Yinxiao ;
Zhang, Youlin .
JOURNAL OF EXPERIMENTAL NANOSCIENCE, 2014, 9 (02) :120-125
[43]   Facile and rapid synthesis of nickel nanowires and their magnetic properties [J].
Shaochun Tang ;
Zhou Zheng ;
Sascha Vongehr ;
Xiangkang Meng .
Journal of Nanoparticle Research, 2011, 13 :7085-7094
[44]   Synthesis and magnetic properties of Mn doped ZnO nanowires [J].
Deka, Sasanka ;
Joy, P. A. .
SOLID STATE COMMUNICATIONS, 2007, 142 (04) :190-194
[45]   The effect of magnetic layer thickness on magnetic properties of Fe/Cu multilayer nanowires [J].
Almasi-Kashi, M. ;
Ramazani, A. ;
Kheyri, F. ;
Jafari-Khamse, E. .
MATERIALS CHEMISTRY AND PHYSICS, 2014, 144 (03) :230-234
[46]   On the sol-gel synthesis and characterization of strontium ferrite ceramic material [J].
Jaiswal, Shivendra Kumar ;
Kashyap, Vijay Kumar ;
Kumar, Jitendra .
MATERIALS RESEARCH BULLETIN, 2012, 47 (03) :692-699
[47]   Synthesis of Vertically Aligned Dense ZnO Nanowires [J].
Gong, Lihong ;
Wu, Xiang ;
Chen, Huibo ;
Qu, Fengyu ;
An, Maozhong .
JOURNAL OF NANOMATERIALS, 2011, 2011
[48]   Structural and magnetic phases in ball milled strontium ferrite [J].
Kaczmarek, WA ;
Campbell, SJ ;
Wu, E ;
Idzikowski, B ;
Muller, KH .
MECHANICALLY ALLOYED, METASTABLE AND NANOCRYSTALLINE MATERIALS, PART 1, 1998, 269-2 :455-460
[49]   Synthesis and magnetic properties of strontium hexaferrite from celestite ore [J].
Hessien, M. M. ;
Rashad, M. M. ;
Hassan, M. S. ;
El-Barawy, K. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 476 (1-2) :373-378
[50]   Effects of Ce Doping on the Structure, Morphology, and Magnetic Properties of M-Type Strontium Ferrite [J].
Pi, Siwen ;
Li, Jie ;
Zhang, Yingde ;
Zhou, Weina ;
Shan, Shuo ;
Zhao, Xuan .
JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, 2024, 37 (11-12) :1801-1813
12345