Synthesis and optimization of the magnetic properties of aligned strontium ferrite nanowires

被引：8
作者：
Ebrahimi, Fatemeh [1 ]
Bakhshi, Saeed Reza [2 ]
Ashrafizadeh, Fakhreddin [1 ]
Ghasemi, Ali [2 ]
机构：
[1] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran
[2] Malek Ashtar Univ Technol, Dept Mat Engn, Shahin Shahr, Iran
来源：
MATERIALS RESEARCH BULLETIN | 2016年 / 76卷
关键词：
Magnetic materials; Nanostructures; Electron microscopy; Sol-gel chemistry; Magnetic properties;
D O I：
10.1016/j.materresbull.2015.11.061
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
High aspect ratio strontium hexaferrite nanowires were fabricated by dip coating in alumina template. Fe/Sr ratio was changed from 10 to 12 in precursor, and the samples were annealed at a range of temperatures 500-900 degrees C in order to optimize the magnetic properties of strontium ferrite in the form of nanowires. Field emission scanning electron microscope (FESEM) proved the formation of nanowires in the templates, while TEM images revealed a high degree of crystallinity. The ferrites were further characterized by X-ray diffraction (XRD) and energy dispersive X-ray spectrometer (EDS). Magnetic properties of the specimens were studied by a SQUID at 10-300 K. The results showed that the coercivity of packed density nanowires in the template was much less than that of the nanopowders. On the other hand, the coercivity of nanowires at ambient temperature was less than low temperature coercivity. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：240 / 246
页数：7
相关论文
共 50 条
[31]   Facile synthesis of hexagonal strontium ferrite nanostructures and hard magnetic poly carbonate nanocomposite [J].
Ahmadi, Ali ;
Ghanbari, Davood ;
Nabiyouni, Gholamreza .
MAIN GROUP METAL CHEMISTRY, 2017, 40 (1-2) :9-18
[32]   A study on the synthesis and magnetic properties of the cerium ferrite ceramic [J].
Jabbarzare, Saeid ;
Abdellahi, Majid ;
Ghayour, Hamid ;
Arpanahi, Asiyeh ;
Khandan, Amirsalar .
JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 694 :800-807
[33]   Cobalt ferrite nanoparticles: Coprecipitation synthesis and magnetic properties [J].
Xu, L ;
Zhang, HT ;
Hong, JM ;
Zou, WQ ;
Zhou, ZP ;
Chen, XT .
CHINESE JOURNAL OF INORGANIC CHEMISTRY, 2005, 21 (05) :741-743
[34]   Nickel ferrite: combustion synthesis, characterization and magnetic properties [J].
Costa, ACFM ;
Gama, L ;
Morelli, MR ;
Kiminami, RHGA .
ADVANCED POWDER TECHNOLOGY IV, 2005, 498-499 :618-623
[35]   Strontium ferrite nanoparticles synthesized in presence of polyvinylalcohol:: Phase composition, microstructural and magnetic properties [J].
Veverka, P. ;
Knizek, K. ;
Pollert, E. ;
Bohacek, J. ;
Vasseur, S. ;
Duguet, E. ;
Portier, J. .
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2007, 309 (01) :106-112
[36]   Analysis of crystal structure and magnetic properties of strontium substituted bismuth ferrite thin films [J].
Pani, Tapan Kumar ;
Sundaray, Bibekananda .
JOURNAL OF PHYSICS-CONDENSED MATTER, 2020, 32 (50)
[37]   Preparation, magnetic and electromagnetic properties of polyaniline/strontium ferrite/multiwalled carbon nanotubes composite [J].
Li, Yuqing ;
Huang, Ying ;
Qi, Shuhua ;
Niu, Lei ;
Zhang, Yinling ;
Wu, Yanfei .
APPLIED SURFACE SCIENCE, 2012, 258 (08) :3659-3666
[38]   Magnetic Nanoparticles: Synthesis, Characterization and Magnetic Properties of Cobalt Aluminum Ferrite [J].
Zaki, H. M. ;
Al-Heniti, Saleh. H. ;
Al-Hadeethi, Y. ;
Alsanoosi, A. M. .
JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2016, 16 (05) :4733-4741
[39]   Fabrication of aligned ferrite nanofibers by magnetic-field-assisted electrospinning coupled with oxygen plasma treatment [J].
Wang, Hang ;
Tang, Hongzhe ;
He, Junhui ;
Wang, Qingwei .
MATERIALS RESEARCH BULLETIN, 2009, 44 (08) :1676-1680
[40]   Facile and rapid synthesis of nickel nanowires and their magnetic properties [J].
Tang, Shaochun ;
Zheng, Zhou ;
Vongehr, Sascha ;
Meng, Xiangkang .
JOURNAL OF NANOPARTICLE RESEARCH, 2011, 13 (12) :7085-7094
12345