Effect of Nb-ion implantation on the oxidation resistance of TiAl

被引：27
|
作者：
Taniguchi, S
Shibata, T
Saeki, T
Zhang, HX
Liu, XH
机构：
[1] BEIJING NORMAL UNIV,INST LOW ENERGY NUCL PHYS,BEIJING 100875,PEOPLES R CHINA
[2] CHINESE ACAD SCI,SHANGHAI INST MET,ION BEAM LAB,SHANGHAI 200050,PEOPLES R CHINA
来源：
MATERIALS TRANSACTIONS JIM | 1996年 / 37卷 / 05期
关键词：
titanium aluminide; oxidation; temperature cycle; high temperature; niobium; implantation; alumina scale;
D O I：
10.2320/matertrans1989.37.998
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The TiAI specimens implanted with Mb ions of a dose of 1.2 x 10(21) m(-2) were subjected to isothermal and cyclic oxidation tests at 1200 K in a flow of purified oxygen under atmospheric pressure. The results were compared with those for Nb-free specimens. The implantation of Nb ions decreases the overall oxidation rate in the both tests. There is no scale spallation from the Nb-implanted specimen during the cyclic oxidation. Two kinds of scales were formed on each specimen: an alumina-rich (virtually alumina) scale and a two-layer scale which has been often observed. The implantation of Nb improves the mechanical integrity of the alumina scale and decreases the growth rate of the two-layer scale.
引用
收藏
页码：998 / 1003
页数：6
相关论文
共 50 条
  • [21] HIGH TEMPERATURE OXIDATION BEHAVIOUR OF TiAl8Nb ALLOY
    Przybylski, K.
    Prazuch, J.
    Brylewski, T.
    Durda, E.
    ARCHIVES OF METALLURGY AND MATERIALS, 2013, 58 (02) : 477 - 480
  • [22] Influence of silicon ion implantation and post-implantation annealing on the oxidation behaviour of TiAl under thermal cycle conditions
    Taniguchi, S
    Kuwayama, T
    Zhu, YC
    Matsumoto, Y
    Shibata, T
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 277 (1-2): : 229 - 236
  • [23] Microstructure and oxidation kinetics of intermetallic TiAl after Si- and Mo- ion implantation
    Hornauer, U
    Richter, E
    Matz, W
    Reuther, H
    Mücklich, A
    Wieser, E
    Möller, W
    Schumacher, G
    Schütze, M
    SURFACE & COATINGS TECHNOLOGY, 2000, 128 : 418 - 422
  • [24] Effects of Cr and Nb on the high temperature oxidation of TiAl
    D. B. Lee
    K. B. Park
    M. Nakamura
    Metals and Materials International, 2002, 8 : 319 - 326
  • [25] Effect of Mo on microstructure and oxidation of NiCoCrAlY coatings on high Nb containing TiAl alloys
    Gong, X.
    Chen, R. R.
    Yang, Y. H.
    Wang, Y.
    Ding, H. S.
    Guo, J. J.
    Su, Y. Q.
    Fu, H. Z.
    APPLIED SURFACE SCIENCE, 2018, 431 : 81 - 92
  • [26] Effects of Cr and Nb on the high temperature oxidation of TiAl
    Lee, DB
    Park, KB
    Nakamura, M
    METALS AND MATERIALS INTERNATIONAL, 2002, 8 (03): : 319 - 326
  • [27] Evaluation of the resistance to oxidation of niobium treated by high temperature nitrogen Plasma Based Ion Implantation
    Oliveira, Rogerio M.
    Hoshida, Lilian
    Oliveira, Aline C.
    Silva, Matheus M. N. F.
    Pichon, Luc
    Santos, Nazir M.
    SURFACE & COATINGS TECHNOLOGY, 2017, 312 : 110 - 116
  • [28] Effect of nanocrystallization on oxidation resistance of TiAl intermetallic compound
    Tang, ZL
    Wang, FH
    Wu, WT
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 1997, 7 (02) : 103 - 107
  • [29] Oxidation Resistance of Ion-Implanted γ-TiAl-Base Intermetallics
    M.K. Lei
    X.P. Zhu
    X.J. Wang
    Oxidation of Metals, 2002, 58 : 361 - 374
  • [30] Oxidation resistance of ion-implanted γ-TiAl-base intermetallics
    Lei, MK
    Zhu, XP
    Wang, XJ
    OXIDATION OF METALS, 2002, 58 (3-4): : 361 - 374
12345