Solubility product and precipitation of TaC in Fe-8Cr-2W steel

被引:36
作者
Tamura, M [1 ]
Shinozuka, K
Masamura, K
Ishizawa, K
Sugimoto, S
机构
[1] Natl Def Acad, Dept Mat Sci, Yokosuka, Kanagawa 239, Japan
[2] NKK Corp, Kawasaki Ku, Kawasaki, Kanagawa 210, Japan
[3] Kokan Keisoku Co, Kawasaki Ku, Kawasaki, Kanagawa 210, Japan
关键词
D O I
10.1016/S0022-3115(98)00151-2
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The precipitation behavior of TaC in austenite was studied to improve mechanical properties of a reduced-activation steel, Type F-82H tan 8%Cr-2%W steel). The solubility product of TaC in austenite of Type F-82H was determined as function of temperature and was 70% larger than that of gamma-Fe. On metallurgical examination, the following was found: (1) The nucleation and growth of austenite grains and/or the reverse alpha --> gamma transformation accelerated the precipitation of fine particles of TaC, and the fine precipitates suppressed the further growth of the austenite grains. (2) When homogenizing at 1523 K previously, coarse austenitic grains were observed by heating at 1223-1323 K as compared with the grains after directly heating of the hot-rolled plate, while the solubility product itself was roughly independent of the homogenizing treatment. (C) 1998 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:1158 / 1162
页数:5
相关论文
共 14 条
  • [1] MODELING OF NBC PRECIPITATION KINETICS IN HOT DEFORMED AUSTENITE ON NB BEARING LOW-CARBON STEELS
    AKAMATSU, S
    MATSUMURA, Y
    SENUMA, T
    YADA, H
    ISHIKAWA, S
    [J]. TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1989, 75 (06): : 933 - 940
  • [2] AKAMATSU S, 1992, TETSU TO HAGANE, V78, P790
  • [3] DUTTA B, 1987, MATER SCI TECH SER, V3, P197, DOI 10.1179/026708387790122846
  • [4] MECHANICAL-PROPERTIES OF WELDED-JOINTS OF THE REDUCED-ACTIVATION FERRITIC STEEL - 8-PERCENT CR-2-PERCENT W-0.2-PERCENT V-0.04-PERCENT TA-FE
    HAYAKAWA, H
    YOSHITAKE, A
    TAMURA, M
    NATSUME, S
    GOTOH, A
    HISHINUMA, A
    [J]. JOURNAL OF NUCLEAR MATERIALS, 1991, 179 : 693 - 696
  • [5] MATSUDA S, 1974, J IRON STEEL I JPN, V60, P226
  • [6] MURATA M, 1988, J IRON STEEL I JPN, V74, P1454
  • [7] NAKAZAWA K, 1981, J IRON STEEL I JPN, V67, P1795
  • [8] Narita K, 1966, KOBE STEEL ENG REPOR, V16, P179
  • [9] OSTWALD RIPENING OF PRECIPITATES IN SOLID MATRICES
    ORIANI, RA
    [J]. ACTA METALLURGICA, 1964, 12 (12): : 1399 - &
  • [10] SEKI Y, 1990, 13 INT C PLASM PHYS