Microstructure and mechanical properties of an extruded γ-TiAlMoSi alloy

被引:5
|
作者
Wesemann, J [1 ]
Frommeyer, G [1 ]
Kruse, J [1 ]
机构
[1] Max Planck Inst Eisenforsch GmbH, D-40237 Dusseldorf, Germany
关键词
titanium aluminides; based on TiAl; plastic deformation mechanisms; twinning; extrusion; microstructure;
D O I
10.1016/S0966-9795(00)00119-9
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Two samples of a two phase gamma/alpha (2)-Ti52A146.8Mo1Si0.2 alloy have been extruded with the reduction ratio in the cross section of 7:1 at 1250 degreesC and the ratio 12.5:1 at 1300 degreesC. Mechanical tests have been performed in the temperature regime from 20 to 1000 degreesC. The sample extruded at 1250 degreesC possesses a microstructure with gamma and alpha (2) grains with grain sizes of less than 3 mum and coarser single-phase gamma grains 10-40 mum in size. The alloy exhibits an excellent balance of ductility and strength. Al room temperature the yield strength is 720 MPa, the elongation to failure is is an element of (pl)=30% The ductility rapidly increases and the yield stress strongly decreases with temperature increases above 700 degreesC. The alloy extruded at 1300 degreesC has a similar microstructure as the alloy extruded at 1250 degreesC, but Lamellar grains exist near the rod axis. The yield strength of this alloy is higher within the considered temperature range, but its ductility is reduced (YS = 807 MPa, is an element of (pl) = 2.6% at room temperature). The loss in yield strength with increasing temperature of the 7:1 extruded TiAlMoSi alloy is much more pronounced than that of the 12.5:1 extruded TiAlMoSi alloy for temperatures higher than 600 degreesC. (C) 2001 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码:273 / 278
页数:6
相关论文
共 50 条
  • [31] Influence of Aging Prior to Extrusion on the Microstructure and Mechanical Properties of an Extruded AZ91 Alloy
    Zhu, Yulin
    Liu, Feiya
    Xin, Renlong
    Song, Bo
    Liu, Qing
    ADVANCED ENGINEERING MATERIALS, 2020, 22 (07)
  • [32] Microstructure and mechanical properties of extruded machined chips for AZ91D magnesium alloy
    Inha Univ, Inchon, Korea, Republic of
    Keikinzoku J Jpn Inst Light Met, 7 (391-396):
  • [33] Effect of Rolling Deformation on the Microstructure and Mechanical Properties of an Extruded Mg-Zn-Ca Alloy
    Du, Yuzhou
    Cheng, Bo
    Shen, Mingjie
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (07) : 4357 - 4363
  • [34] Effect of Cu Addition on the Microstructure and Mechanical Properties of an As-Extruded ZK60 Alloy
    Park, Sung Hyuk
    Yu, Hui
    Kim, Ha Sik
    Bae, Jun Ho
    Yim, Chang Dong
    You, Bong Sun
    KOREAN JOURNAL OF METALS AND MATERIALS, 2013, 51 (03): : 169 - 179
  • [35] Microstructure and mechanical properties of extruded Mg96Zn1Y3 alloy
    Li, R. G.
    Zhang, H. J.
    Fu, G. Y.
    MATERIALS CHARACTERIZATION, 2014, 98 : 107 - 112
  • [36] Microstructure and Mechanical Properties of Rheo-Extruded AZ31 Mg-alloy
    Xu, Jun
    Zhang, Shaoming
    Yang, Bicheng
    Shi, Likai
    Fan, Z.
    SEMI-SOLID PROCESSING OF ALLOYS AND COMPOSITES X, 2008, 141-143 : 713 - +
  • [37] Effects of Al addition on microstructure and mechanical properties of extruded Mg-3Bi alloy
    Jin, Sang-Cheol
    Cha, Jae Won
    Bae, Jun Ho
    Yu, Hui
    Park, Sung Hyuk
    JOURNAL OF MAGNESIUM AND ALLOYS, 2022, 10 (07) : 1887 - 1898
  • [38] Microstructure, Texture and Mechanical Properties of Mg-Zn-Ce Alloy Extruded at Different Temperatures
    Chino, Yasumasa
    Huang, Xinsheng
    Suzuki, Kazutaka
    Sassa, Kensuke
    Mabuchi, Mamoru
    MATERIALS TRANSACTIONS, 2011, 52 (06) : 1104 - 1107
  • [39] Effects of heat treatment on microstructure and mechanical properties of extruded AZ80 magnesium alloy
    Zhao, Degang
    Wang, Zhenqing
    Zuo, Min
    Geng, Haoran
    MATERIALS & DESIGN, 2014, 56 : 589 - 593
  • [40] MICROSTRUCTURE AND MECHANICAL PROPERTIES OF EXTRUDED Mg-2Y-1Zn MAGNESIUM ALLOY
    Dvorsky, Drahomir
    Kubasek, Jiri
    Vojtech, Dalibor
    Vavrik, Jaroslav
    METAL 2017: 26TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2017, : 1519 - 1523