Failure of navy coating systems 1: chemical depth profiling of artificially and naturally weathered high-solids aliphatic poly(ester-urethane) military coating systems

被引：10

作者：

Keene, LT ^{[1
]}

Halada, GP ^{[1
]}

Clayton, CR ^{[1
]}

机构：

[1] SUNY Stony Brook, Dept Mat Sci & Engn, Stony Brook, NY 11794 USA

来源：

PROGRESS IN ORGANIC COATINGS | 2005年 / 52卷 / 03期

关键词：

depth-profile; FT-IR; polyurethane; pigment; UV;

D O I：

10.1016/j.porgcoat.2004.11.004

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

A variety of weathering protocols are in use in industry and research laboratories to both replicate and accelerate the effects of weathering on coating systems. This work focuses on the use of two artificial and one natural weathering protocol (QUV, GM9540P, Florida beach exposure) in combination with spatially resolved transmission-mode Fourier transform infrared (FT-IR) spectroscopy for the purpose of chemically depth-profiling highly opaque high solids multi-layer poly(ester-urethane) coatings employed by the U.S. Department of Defense. Samples were prepared via subjection to 6/12-week GM9540P exposure, 7/13/25-week Florida beach exposure, or 6-/8-week QUV protocol. Thin (3 mu m) cross-section samples were prepared via microtomy and depth-dependant trends in chemical evolutions were analyzed using transmission-mode micro-FT-IR. Scanning electron/energy-dispersive microscopy (SEM/EDS) was conducted on 10 mu m cross-sections and spatial distribution/chemical makeup of inorganic constituents were analyzed. An apparent synergistic relationship between weathering protocols was found. It was theorized that a combination of chemistry and morphology of the inorganic fillers was primarily responsible for greater-than-expected photooxidative modification of the polymeric binder. Published by Elsevier B.V.

引用

页码：173 / 186

页数：14

共 25 条

[21] Two package waterborne urethane systems [J].

Wicks, ZW ;

Wicks, DA ;

Rosthauser, JW .

PROGRESS IN ORGANIC COATINGS, 2002, 44 (02) :161-183

[22] Infrared analysis of the photochemical behaviour of segmented polyurethanes .1. Aliphatic poly(ester-urethane) [J].

Wilhelm, C ;

Gardette, JL .

POLYMER, 1997, 38 (16) :4019-4031

[23] Degradation of low gloss polyurethane aircraft coatings under UV and prohesion alternating exposures [J].

Yang, XF ;

Li, J ;

Croll, SG ;

Tallman, DE ;

Bierwagen, GP .

POLYMER DEGRADATION AND STABILITY, 2003, 80 (01) :51-58

[24] Blistering and degradation of polyurethane coatings under different accelerated weathering tests [J].

Yang, XF ;

Tallman, DE ;

Bierwagen, GP ;

Croll, SG ;

Rohlik, S .

POLYMER DEGRADATION AND STABILITY, 2002, 77 (01) :103-109

[25] Weathering degradation of a polyurethane coating [J].

Yang, XF ;

Vang, C ;

Tallman, DE ;

Bierwagen, GP ;

Croll, SG ;

Rohlik, S .

POLYMER DEGRADATION AND STABILITY, 2001, 74 (02) :341-351

← 1 2 3 →