Propagation of physically short cracks in a bainitic high strength bearing steel due to fatigue load

被引：12

作者：

Alfredsson, B. ^{[1
]}

Oberg, M. ^{[1
]}

Lai, J. ^{[2
]}

机构：

[1] Royal Inst Technol KTH, Dept Solid Mech, S-10044 Stockholm, Sweden

[2] SKF Engn & Res Ctr, POB 2350, NL-3430 DT Nieuwegein, Netherlands

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2016年 / 90卷

关键词：

Fatigue crack experiment; Short crack growth; Crack closure; Life prediction; Potential drop; GROWTH; BEHAVIOR; CLOSURE;

D O I：

10.1016/j.ijfatigue.2016.04.031

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Physically short cracks in a bainitic high strength bearing steel were fatigue loaded. The rapid propagation rate of early open short cracks agreed with that of long closure free cracks. After some rapid growth, the short cracks entered a transition period to the rate of growth limited long cracks. Potential drop showed that the short cracks were open to the tip throughout the growth sequence, which excluded crack face closure in the wake as the growth limiting mechanism in this material. Instead the short crack effect was related to residual stresses and other mechanisms at the crack tip. Crack manufacturing procedures were determined for straight long and short start cracks in the present material. LEFM with effective material parameters and limit compensation predicted the short crack lives. (C) 2016 Elsevier Ltd. All rights reserved.

引用

页码：166 / 180

页数：15

共 40 条

[1] Fatigue crack initiation and growth at holes in a high strength bainitic roller bearing steel when loaded with non-proportional shear and compressive cycles
Alfredsson, Bo
Watz, Veronica
Olsson, Erik
[J]. INTERNATIONAL JOURNAL OF FATIGUE, 2011, 33 (09) : 1244 - 1256
[2] [Anonymous], 2011, D176284 ASTM
[3] [Anonymous], 2012, ASTM D882
[4] Non-linear elastic characterisation of a high strength bainitic roller bearing steel
Arregui, I. Linares
Alfredsson, B.
[J]. INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2013, 68 : 1 - 15
[5] Elastic-plastic characterization of a high strength bainitic roller bearing steel-experiments and modelling
Arregui, I. Linares
Alfredsson, B.
[J]. INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2010, 52 (10) : 1254 - 1268
[6] FRACTURE AND FATIGUE CRACK-PROPAGATION PROPERTIES OF HARDENED 52100 STEEL
BESWICK, JM
[J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (10): : 1961 - 1973
[7] Steels for bearings
Bhadeshia, H. K. D. H.
[J]. PROGRESS IN MATERIALS SCIENCE, 2012, 57 (02) : 268 - 435
[8] Bhadeshia HKDH, 2001, BAIN STEELS TRANSF M
[9] Fatigue growth of short cracks in Ti-17: Experiments and simulations
Cadario, A.
Alfredsson, B.
[J]. ENGINEERING FRACTURE MECHANICS, 2007, 74 (15) : 2293 - 2310
[10] CHANG LC, 1995, MATER SCI TECH SER, V11, P874, DOI 10.1179/026708395790165462

← 1 2 3 4 →