Effect of O2 on corrosion of 3Cr steel in high temperature and high pressure CO2-O2 environment

被引:67
作者
Lin, Xueqiang [1 ]
Liu, Wei [1 ]
Wu, Fei [1 ]
Xu, Chuanchuan [1 ]
Dou, Juanjuan [1 ]
Lu, Minxu [1 ]
机构
[1] Univ Sci & Technol Beijing, Corros & Protect Ctr, Inst Adv Mat & Technol, Beijing 100083, Peoples R China
关键词
3Cr steel; SEM; EIS; O-2; corrosion; CO2; Pitting corrosion; CARBON-DIOXIDE; CHROMIUM; CO2; BEHAVIOR; RESISTANCE; OXYGEN;
D O I
10.1016/j.apsusc.2014.12.109
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The development of corrosion scale of 3Cr steel in an aqueous environment containing 95% CO2-5% O-2 was characterized and analyzed by scanning electron microscopy (SEM), energy-dispersive spectrometry (EDS), X-ray diffraction (XRD) and in situ electrochemical impedance spectroscopy (EIS). The results show that the corrosion of 3Cr steel was promoted by dissolved oxygen. Fe(OH)(3) precipitation formed at local areas, leading to the nonuniform distribution of Cr element and pitting corrosion. With the increase of corrosion time, Cr-rich area formed at the bottom of pits, where the pitting corrosion process was inhibited. The importance of Fe(OH)(3) and Cr-rich area on the formation of corrosion pits and pits development was emphasized. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码:104 / 115
页数:12
相关论文
共 32 条
  • [1] Corrosion rate of iron and iron-chromium alloys in CO2 medium
    Carvalho, DS
    Joia, CJB
    Mattos, OR
    [J]. CORROSION SCIENCE, 2005, 47 (12) : 2974 - 2986
  • [2] Effect of chromium on the pitting resistance of oil tube steel in a carbon dioxide corrosion system
    Chen, CF
    Lu, MX
    Sun, DB
    Zhang, ZH
    Chang, W
    [J]. CORROSION, 2005, 61 (06) : 594 - 601
  • [3] Chen T., 2011, CORR 2011
  • [4] Durr C., 1996, CORR 1996
  • [5] Evolution of dissolution processes at the interface of carbon steel corroding in a CO2 environment studied by EIS
    Farelas, F.
    Galicia, M.
    Brown, B.
    Nesic, S.
    Castaneda, H.
    [J]. CORROSION SCIENCE, 2010, 52 (02) : 509 - 517
  • [6] Corrosion of alloy steels containing 2% chromium in CO2 environments
    Guo, Shaoqiang
    Xu, Lining
    Zhang, Lei
    Chang, Wei
    Lu, Minxu
    [J]. CORROSION SCIENCE, 2012, 63 : 246 - 258
  • [7] Evolution of atmospheric corrosion of MnCuP weathering steel in a simulated coastal-industrial atmosphere
    Hao, Long
    Zhang, Sixun
    Dong, Junhua
    Ke, Wei
    [J]. CORROSION SCIENCE, 2012, 59 : 270 - 276
  • [8] Effect of silicon on the oxidation resistance of 9% Cr steels
    Huntz, AM
    Bague, V
    Beauplé, G
    Haut, C
    Sévérac, C
    Lecour, P
    Longaygue, X
    Ropital, F
    [J]. APPLIED SURFACE SCIENCE, 2003, 207 (1-4) : 255 - 275
  • [9] Ikeda A., 1994, CO 2 CORROSION BEHAV, P59
  • [10] Jackson T, 2009, CORR 1996