Development of structural ceramics having large crack-healing ability and fracture toughness

被引：0
作者：
Takahashi, K [1 ]
Yokouchi, M [1 ]
Lee, SK [1 ]
Ando, K [1 ]
机构：
[1] Yokohama Natl Univ, Yokohama, Kanagawa 2408501, Japan
来源：
SMART MATERIALS III | 2005年 / 5648卷
关键词：
crack healing; alumina; SiC whiskers; fracture toughness;
D O I：
10.1117/12.580719
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Al2O3 reinforced by SiC whiskers (Al2O3/SiC-W) was hot pressed to investigate the crack-healing behavior. Semi-elliptical surface cracks of 50 to 450 mu m in surface length were introduced using a Vickers indenter. The specimens containing pre-cracks were crack-healed at temperatures between 1000 degrees C and 1300 degrees C for 1h in air, and their strengths were measured by three-point bending tests at room temperature and elevated temperatures between 400 degrees C and 1300 degrees C. The results show that Al2O3/SiC-W possesses considerable crack-healing ability. The surface cracks with length of 2c = 100 mu m. could be healed by crack-healing at 1200 degrees C or 1300 degrees C. for 1h in air. The maximum crack size that can be healed for Al2O3/SiC-W is 2c = 200 mu m. Fracture toughness of the material was also determined. As expected, the SiC whiskers made their Al2O3 tougher.
引用
收藏
页码：276 / 283
页数：8
相关论文
共 50 条
  • [31] Crack-healing Behavior of Al2O3/SiC composite ceramics and the bending strength of crack-healed body
    Ando, K
    Kim, BS
    Chu, MC
    Saitou, S
    Sato, S
    [J]. ADVANCED CERAMICS AND COMPOSITES, 2003, 247 : 175 - 178
  • [32] Crack-healing during two-stage crystallization of biomedical lithium (di)silicate glass-ceramics
    Belli, Renan
    Lohbauer, Ulrich
    Goetz-Neunhoeffer, Friedlinde
    Hurle, Katrin
    [J]. DENTAL MATERIALS, 2019, 35 (08) : 1130 - 1145
  • [33] Mechanical Characteristics and Crack-Healing of ZIRCONIA(ZrO2) Composite Ceramics with SiC and TiO2
    Nam, Ki Woo
    [J]. TRANSACTIONS OF THE KOREAN SOCIETY OF MECHANICAL ENGINEERS A, 2016, 40 (03) : 267 - 273
  • [34] A methodology to increase a strength and guarantee a reliability of an Al2O3/SiC composite ceramics component by crack-healing and proof testing
    Ono, Masato
    Nakao, Wataru
    Takahashi, Koji
    Ando, Kotoji
    [J]. JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2007, 115 (1348) : 967 - 973
  • [35] Failure from large grains in polycrystalline ceramics: Transitions in fracture toughness
    Freiman, S
    [J]. FRACTURE RESISTANCE TESTING OF MONOLITHIC AND COMPOSITE BRITTLE MATERIALS, 2002, 1409 : 17 - 29
  • [36] Large anisotropy of fracture toughness in mechanicafly poled/depoled ferroelectric ceramics
    Li, Y. W.
    Li, F. X.
    [J]. SCRIPTA MATERIALIA, 2010, 62 (05) : 313 - 316
  • [37] Estimation of fracture toughness in ZnO ceramics from indentation crack opening displacement measurements
    Roy, Tapatee Kundu
    [J]. MEASUREMENT, 2019, 137 : 588 - 594
  • [38] Influences of Crack Face Bridging Stress and Microstructure on Fracture Toughness of Toughened Alumina Ceramics
    Sakaida, Yoshihisa
    Yoshida, Hajime
    Mori, Shotaro
    [J]. FRACTURE AND STRENGTH OF SOLIDS VII, PTS 1 AND 2, 2011, 462-463 : 972 - 978
  • [39] Fracture toughness and crack deflection in porous multilayered ceramics: application to NiO-YSZ
    Joulaee, N.
    Makradi, A.
    Ahzi, S.
    Khaleel, A.
    [J]. DIFFUSION IN SOLIDS AND LIQUIDS: HEAT TRANSFER - MICROSTRUCTURE & PROPERTIES, 2007, 553 : 69 - +
  • [40] Crack-healing behavior of Si3N4/SiC ceramics under stress and fatigue strength at the temperature of healing (1000°C)
    Ando, K
    Houjyou, K
    Chu, MC
    Takeshita, S
    Takahashi, K
    Sakamoto, S
    Sato, S
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (08) : 1339 - 1346
12345