Effect of intermetallics on susceptibility of Mg alloy welds to liquation cracking

被引：10

作者：

Yuan, Tao ^{[1
,2
]}

Yu, Zhanliang ^{[1
,2
]}

Wang, Xuan ^{[1
,2
]}

Chen, Shujun ^{[1
,2
]}

机构：

[1] Beijing Univ Technol, Welding Res Inst, Minist Educ, Beijing, Peoples R China

[2] Beijing Univ Technol, Engn Res Ctr Adv Mfg Technol Automot Components, Minist Educ, Beijing, Peoples R China

来源：

SCIENCE AND TECHNOLOGY OF WELDING AND JOINING | 2020年 / 25卷 / 06期

关键词：

Magnesium alloys; intermetallic compounds; liquation cracking; heat treatment; MECHANICAL-PROPERTIES; HEAT-TREATMENT; HOT CRACKING; MAGNESIUM; MICROSTRUCTURE; ZONE;

D O I：

10.1080/13621718.2020.1747198

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The circular-patch welding test was used to study the liquation and liquation cracking of AZ-series Mg alloys. A heat treatment was carried out on the as-received AZ91 alloy to dissolve the gamma(Mg17Al12) particles before welding. The circular-patch welding test was then conducted on the heat-treated, as-received AZ91 alloy using AZ61 and AZ91 filler wires. The results showed that the susceptibility of AZ91 alloy to liquation and liquation cracking was significantly reduced by the dissolution of massive gamma(Mg17Al12) particles via a heat treatment before welding as the liquation mechanism was changed. Both constitutional liquation and incipient melting occurred in the partially melted zone of the as-received AZ91 welds, while only incipient melting occurred in the heat-treated AZ91 welds.

引用

页码：496 / 502

页数：7

共 50 条

[31] Investigation on liquation cracks of dissimilar magnesium alloy welds using the circular-patch experiment and numerical simulation
Yuan, Tao
Zhang, Hongda
Jiang, Xiaoqing
Chen, Shujun
Xu, Min
Liu, Xusheng
JOURNAL OF MANUFACTURING PROCESSES, 2022, 75 : 49 - 59
[32] Suppression of liquation cracking susceptibility via pre-weld heat treatment for manufacturing of CM247LC superalloy turbine blade welds
Chun, Eun-Joon
Jeong, Ye-Seon
Kim, Kyeong-Min
Lee, Hyungsoo
Seo, Seong-Moon
JOURNAL OF ADVANCED JOINING PROCESSES, 2021, 4
[33] Influence of electron beam welding parameters and metallurgical factors on intergranular liquation cracking susceptibility of cast alloy 718
Insu Woo
Chungyun Kang
Kazutoshi Nishimoto
Metals and Materials International, 2001, 7 : 349 - 357
[34] Experimental and numerical analysis of intermetallics in Al-Mg friction stir welds
Naveenkumar, M.
Subramanian, M.
Ranjith, R.
MATERIALS RESEARCH EXPRESS, 2023, 10 (11)
[35] Effects of polarisation on mechanical properties and stress corrosion cracking susceptibility of 7050 aluminium alloy
Qi, X.
Song, R. G.
Qi, W. J.
Jin, J. R.
Wang, C.
Li, H.
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2014, 49 (07) : 643 - 650
[36] Effect of Postweld Heat Treatment on the Sulfide Stress Cracking of Dissimilar Welds of Nickel-Based Alloy 625 on Steels
Dai, Tao
Thodla, Ramgopal
Kovacs, William, III
Tummala, Kavitha
Lippold, John
CORROSION, 2019, 75 (06) : 641 - 656
[37] Liquation cracking in laser beam welded joint of ZK60 magnesium alloy
Yu Zhao-hui
Yan Hong-ge
Yin Xu-yu
Li Ying
Yan Guo-hua
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2012, 22 (12) : 2891 - 2897
[38] Effect of cooling rate and Co content on the formation of Fe-rich intermetallics in hypoeutectic A17Si0.3Mg alloy with 0.5%Fe
Wu, Xiaoyan
Zhang, Huarui
Zhang, Fengxiang
Ma, Zhen
Jia, Lina
Yang, Bo
Tao, Tongxiang
Zhang, Hu
MATERIALS CHARACTERIZATION, 2018, 139 : 116 - 124
[39] Relative Volta Potentials of Intermetallics in AZ91-RE Mg Alloy After Solution and Aging Treatment
Ding, Yanfang
Jia, Ruiling
Zhang, Wei
Zhang, Huixia
Hou, Jian
JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2019, 19 (01) : 188 - 193
[40] Effect of Nd:YAG pulsed laser welding process on the liquation and strain-age cracking in GTD-111 superalloy
Zhang, Guiju
Xiao, Caiyuan
Taheri, Morteza
JOURNAL OF MANUFACTURING PROCESSES, 2020, 52 : 66 - 78

← 1 2 3 4 5 →