Nitrided layer embrittlement due to edge effect on duplex treated AISI M2 high-speed steel

被引:38
作者
Kwietniewski, C
Fontana, W
Moraes, C
Rocha, AD
Hirsch, T
Reguly, A
机构
[1] Univ Val Rio Sinos, Mat Characterisat Grp, ACA Mecan, Sao Leopoldo, Brazil
[2] Inst Werkstoffetech, Bremen, Germany
[3] Univ Fed Rio Grande Sul, Post Grad Program Min Met & Mat Engn, BR-90046900 Porto Alegre, RS, Brazil
关键词
plasma nitriding; TiN hard coating; duplex treatment; nitrided case embrittlement; edge effect;
D O I
10.1016/S0257-8972(03)00795-3
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Plasma nitriding prior to TiN deposition on single-point turning tools made of high-speed steel (HSS) AISI M2 has been carried out in order to investigate the improvement of machining performance. Optical and scanning electron microscopy, microhardness test, glow discharge optical emission spectroscopy (GDOES) and X-ray diffraction (XRD) were used to characterize the nitrided layer. Machining tests using a tool life criterion of 0.3 mm average width of the flank wear land were carried out to,9 evaluate the service performance of the composite tools. The results have indicated that careful attention must be taken when comparing flat coupons to complex shaped substrates. In plasma nitriding systems without. auxiliary heating, nitrogen incorporation depends on the plasma current density and, therefore, temperature, Which can be significantly higher at the tool edges, forming an excessive deep and brittle diffusion case, reducing the service life of the duplex treated tool. The results also indicated that using brighter plasma nitriding, the TiN hard coating machining performance could be improved dramatically. (C) 2003 Elsevier B.V. All rights reserved.
引用
收藏
页码:27 / 32
页数:6
相关论文
共 18 条
[1]   Effect of workpiece geometry on the uniformity of nitrided layers [J].
Alves, C ;
da Silva, EF ;
Martinelli, AE .
SURFACE & COATINGS TECHNOLOGY, 2001, 139 (01) :1-5
[2]  
[Anonymous], 1993, 3685 ISO
[3]   Realising the potential of duplex surface engineering [J].
Bell, T ;
Dong, H ;
Sun, Y .
TRIBOLOGY INTERNATIONAL, 1998, 31 (1-3) :127-137
[4]  
HAUK V, 1997, STRUCTURAL RESIDUAL, P338
[5]   PROCESS TECHNOLOGICAL ASPECTS OF THE PRODUCTION AND PROPERTIES OF IN-SITU COMBINED PLASMA-NITRIDED AND PVD HARD-COATED HIGH-ALLOY TOOL STEELS [J].
HOCK, K ;
LEONHARDT, G ;
BUCKEN, B ;
SPIES, HJ ;
LARISCH, B .
SURFACE & COATINGS TECHNOLOGY, 1995, 74-5 (1-3) :339-344
[6]   Fatigue behavior of duplex treated TiCxN1-x- and Ti1-xAlxN-hard coating steel compounds [J].
Jaeger, G ;
Endler, I ;
Bartsch, K ;
Heilmaier, M ;
Leonhardt, A .
SURFACE & COATINGS TECHNOLOGY, 2002, 150 (2-3) :282-289
[7]   The composite of nitrided steel of H13 and TiN coatings by plasma duplex treatment and the effect of pre-nitriding [J].
Ma, SL ;
Li, YH ;
Xu, KW .
SURFACE & COATINGS TECHNOLOGY, 2001, 137 (2-3) :116-121
[8]  
Macherauch E., 1961, Zeitschrift Fur Angew. Phys, V13, P305
[9]   PLASMA-BASED SURFACE ENGINEERING PROCESSES FOR WEAR AND CORROSION PROTECTION [J].
MATTHEWS, A ;
LEYLAND, A ;
DORN, B ;
STEVENSON, PR ;
BINSUDIN, M ;
REBHOLZ, C ;
VOEVODIN, A ;
SCHNEIDER, J .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1995, 13 (03) :1202-1207
[10]   HYBRID TECHNIQUES IN SURFACE ENGINEERING [J].
MATTHEWS, A ;
LEYLAND, A .
SURFACE & COATINGS TECHNOLOGY, 1995, 71 (02) :88-92