Application of polystyrene as binder for veneers bonding-the effect of pressing parameters

被引：16

作者：

Borysiuk, P. ^{[1
]}

Maminski, M. L. ^{[1
]}

Parzuchowski, P. ^{[2
]}

Zado, A. ^{[1
]}

机构：

[1] Warsaw Univ Life Sci SGGW, Fac Wood Technol, PL-02776 Warsaw, Poland

[2] Warsaw Univ Technol, Fac Chem, PL-00664 Warsaw, Poland

来源：

EUROPEAN JOURNAL OF WOOD AND WOOD PRODUCTS | 2010年 / 68卷 / 04期

关键词：

Shear Strength; Pressing Regime; Wood Plastic Composite; Tensile Shear Strength; Lower Bonding Strength;

D O I：

10.1007/s00107-010-0418-x

中图分类号：

S7 [林业];

学科分类号：

0829 ; 0907 ;

摘要：

The possibility of veneer bonding with recycled polystyrene was examined. Five pressing regimes were studied. It was shown that low-pressure pre-heating is a necessary step allowing for increasing final shear strength of the wood-thermoplastic joints and avoiding indentation of thermoplastic particles to wood.

引用

页码：487 / 489

页数：3

共 8 条

[1] [Anonymous], 2005, 205 EN
[2] Borysiuk P, 2006, P COST ACT E44 49 WO, P277
[3] Vibrational properties of wood plastic plywood
Hu, YC
Nakao, T
Nakai, T
Gu, JY
Wang, FH
[J]. JOURNAL OF WOOD SCIENCE, 2005, 51 (01) : 13 - 17
[4] Pawlicki J., 2002, P WORKSH INN MAT BAS
[5] PRITCHARD G, 2004, REINFORCED PLASTICS, V6, P26
[6] Wood fiber/polyolefin composites
Selke, SE
Wichman, I
[J]. COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2004, 35 (03) : 321 - 326
[7] *TANGR TECHN LTD, 2002, 0104 COM1 TANGR TECH
[8] Youngquist J. A, 1994, COMPOSITES RECYCLED

← 1 →