Influence of embedded ZnAlCe-NO3- layered double hydroxides on the anticorrosion properties of sol-gel coatings for aluminum alloy

被引：49
作者：
Liu, Jianhua [1 ]
Zhang, You [1 ]
Yu, Mei [1 ]
Li, Songmei [1 ]
Xue, Bing [1 ]
Yin, Xiaolin [1 ]
机构：
[1] Beihang Univ, Sch Mat Sci & Engn, Beijing 100191, Peoples R China
来源：
PROGRESS IN ORGANIC COATINGS | 2015年 / 81卷
基金：
中国国家自然科学基金;
关键词：
Layered double hydroxides; Sol-gel coatings; Cerium; Corrosion protection; AA2024; HYDROTALCITE CONVERSION FILM; ACTIVE CORROSION PROTECTION; IN-SITU GROWTH; AL; INHIBITOR; MECHANISM; CE; RESISTANCE; AA2024-T3; PIGMENTS;
D O I：
10.1016/j.porgcoat.2014.12.015
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
A protective coating was designed by dispersing Ce-doped ZnAl layered double hydroxides (ZnAlCe-LDHs) nanoparticles in hybrid sol-gel (SiOx/ZrOx) layer on aluminum alloy AA2024. The concentration of cerium in synthesized LDHs was varied to ascertain the optimum condition for anticorrosion performance. The LDH nanoparticles were characterized in terms of structure, morphology and chemical composition. It was found that Ce (III) was inserted into the sheets of LDHs and two mixture phases of LDHs and CeO2 were formed when the atomic ratio of Ce/(Al + Ce) was higher than 0.05. The sol-gel coating embedded with LDHs (Ce/(Al + Ce)=0.1) exhibited high corrosion resistance, probably due to the synergistic inhibition of ZnAlCe-LDHs and CeO2 nanoparticles. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码：93 / 100
页数：8
相关论文
共 35 条
  • [31] Study on the photochromism of Ni-Al layered double hydroxides containing nitrate anions
    Wei, Min
    Xu, Xiangyu
    Wang, Xinrui
    Li, Feng
    Zhang, Hui
    Lu, Yanluo
    Pu, Min
    Evans, David G.
    Duan, Xue
    [J]. EUROPEAN JOURNAL OF INORGANIC CHEMISTRY, 2006, (14) : 2831 - 2838
  • [32] Anion-exchange inhibition of filiform corrosion on organic coated AA2024-T3 aluminum alloy by hydrotalcite-like pigments
    Williams, G
    McMurray, HN
    [J]. ELECTROCHEMICAL AND SOLID STATE LETTERS, 2003, 6 (03) : B9 - B11
  • [33] Mechanism of corrosion inhibition of AA2024 by rare-earth compounds
    Yasakau, KA
    Zheludkevich, ML
    Lamaka, SV
    Ferreira, MGS
    [J]. JOURNAL OF PHYSICAL CHEMISTRY B, 2006, 110 (11) : 5515 - 5528
  • [34] Active protection coatings with layered double hydroxide nanocontainers of corrosion inhibitor
    Zheludkevich, M. L.
    Poznyak, S. K.
    Rodrigues, L. M.
    Raps, D.
    Hack, T.
    Dick, L. F.
    Nunes, T.
    Ferreira, M. G. S.
    [J]. CORROSION SCIENCE, 2010, 52 (02) : 602 - 611
  • [35] Nanostructured sol-gel coatings doped with cerium nitrate as pre-treatments for AA2024-T3 - Corrosion protection performance
    Zheludkevich, ML
    Serra, R
    Montemor, MF
    Yasakau, KA
    Salvado, IMM
    Ferreira, MGS
    [J]. ELECTROCHIMICA ACTA, 2005, 51 (02) : 208 - 217
1234