Effect of Pre-treatment on the Bi-2223/Ag Tapes Fabricated with Different Powders

被引：0
作者：
Li Mingya [1 ]
Chen Xingpin [2 ]
Ye Chengli
Yu Liang
Zhu Xu
机构：
[1] NE Univ Qinhuangdao, Dept Mat Sci & Engn, Qinhuangdao 066004, Peoples R China
[2] Chongqing Univ, Chongqing 400044, Peoples R China
来源：
RARE METAL MATERIALS AND ENGINEERING | 2011年 / 40卷
关键词：
pre-treatment; Bi-2223/Ag tapes; lead oxide compounds; critical current; CRITICAL-CURRENT DENSITY; PHASE-FORMATION; MICROSTRUCTURE;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Samples of Bi-2223/Ag tapes fabricated with powders contained different lead oxide compounds were annealed at a temperature lower than the formation temperature of Bi-2223 phase before traditional heat treatment, which was called pretreatment. In pre-treatment stage, samples were heat treated at 780 degrees C in 8.5% O-2, and the dwelling time is different. Experimental results show that pre-treatment had different influence on the formation and size of the Bi-2223 grains for tapes fabricated with powders contained different lead oxide compounds. For tapes contained both Ca2PbO4 and the 3321 phase, the decomposition of the 3321 phase enhanced the growth of Bi-2212 grains during pre-treatment process, which promoted the formation of Bi-2223 phase and enhanced the superconducting properties of Bi-2223/Ag tapes.
引用
收藏
页码：325 / 328
页数：4
相关论文
共 50 条
  • [41] Improved uniformity of microstructure and electrical properties of Bi-2223/Ag superconducting tapes
    Guo, YC
    Chen, WM
    Liu, HK
    Dou, SX
    Lukashenko, AV
    PHYSICA C, 2001, 355 (1-2): : 163 - 171
  • [42] Evidence for enhanced grain connectivity due to second phase reduction of Bi-2223/Ag tapes
    Lehndorff, B
    Hardenbicker, P
    Hortig, M
    Piel, H
    PHYSICA C, 1999, 312 (1-2): : 105 - 111
  • [43] Superconducting joint of reacted Bi-2223/Ag multi-filamentary tapes
    Oh, SS
    Ha, HS
    Kim, SC
    Ha, DW
    Kwon, YK
    Ryu, KS
    Joo, J
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2001, 11 (01) : 2998 - 3001
  • [44] The effect of intermediate deformation by eccentric rolling on the Jc(B) performance of multicore Bi-2223/Ag tapes
    Kovác, P
    Huang, YB
    Husek, I
    Spiller, DM
    Bukva, P
    PHYSICA C, 2001, 356 (1-2): : 53 - 61
  • [45] Properties and Microstructuresof Three Kinds of Silversheathed Bi-2223 Tapes
    曾荣
    周贻茹
    叶斌
    周敏
    张建国
    王俊升
    刘安生
    李镇恒
    袁冠森
    RARE METALS, 1994, (01) : 63 - 66
  • [46] Effect of lead oxide compounds on microstructure and critical current density of (Bi,Pb)-2223/Ag tapes
    Li, MY
    Song, Y
    Qu, TM
    Han, Z
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 426 : 1164 - 1169
  • [47] A comparison of strain effect on critical current in Bi-2223 superconducting tapes in different bending modes
    Shin, HS
    Choi, SY
    Ko, DK
    Ha, HS
    Ha, DW
    Oh, SS
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2003, 13 (02) : 3526 - 3529
  • [48] Influence of Packing Atmosphere on the Microstructures and Transport Properties of Bi-2223/AgAu Tapes
    Ma, Xiaobo
    Zhang, Shengnan
    Yu, Zeming
    Liu, Guoqing
    Li, Chengshan
    Li, Jinshan
    Zhang, Pingxiang
    JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, 2019, 32 (08) : 2391 - 2396
  • [49] Effect of mechanical loading on the Ic degradation behavior of Bi-2223 tapes
    Baldan, CA
    Shigue, CY
    Ruppert, E
    Oliveira, UR
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2005, 15 (02) : 3552 - 3555
  • [50] The influence of electroplastic rolling on the mechanical deformation and phase evolution of Bi-2223/Ag tapes
    Lu, Yongjin
    Qu, Timing
    Zeng, Pan
    Lei, Liping
    Fang, Gang
    Sun, Jianfeng
    JOURNAL OF MATERIALS SCIENCE, 2010, 45 (13) : 3514 - 3519
12345