Effect of Pre-treatment on the Bi-2223/Ag Tapes Fabricated with Different Powders

被引：0
作者：
Li Mingya [1 ]
Chen Xingpin [2 ]
Ye Chengli
Yu Liang
Zhu Xu
机构：
[1] NE Univ Qinhuangdao, Dept Mat Sci & Engn, Qinhuangdao 066004, Peoples R China
[2] Chongqing Univ, Chongqing 400044, Peoples R China
来源：
RARE METAL MATERIALS AND ENGINEERING | 2011年 / 40卷
关键词：
pre-treatment; Bi-2223/Ag tapes; lead oxide compounds; critical current; CRITICAL-CURRENT DENSITY; PHASE-FORMATION; MICROSTRUCTURE;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Samples of Bi-2223/Ag tapes fabricated with powders contained different lead oxide compounds were annealed at a temperature lower than the formation temperature of Bi-2223 phase before traditional heat treatment, which was called pretreatment. In pre-treatment stage, samples were heat treated at 780 degrees C in 8.5% O-2, and the dwelling time is different. Experimental results show that pre-treatment had different influence on the formation and size of the Bi-2223 grains for tapes fabricated with powders contained different lead oxide compounds. For tapes contained both Ca2PbO4 and the 3321 phase, the decomposition of the 3321 phase enhanced the growth of Bi-2212 grains during pre-treatment process, which promoted the formation of Bi-2223 phase and enhanced the superconducting properties of Bi-2223/Ag tapes.
引用
收藏
页码：325 / 328
页数：4
相关论文
共 50 条
  • [31] Reactivity and oxygen diffusion property of resistive barriers for Bi-2223/Ag tapes
    Kovác, P
    Husek, I
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 383 (1-2): : 55 - 58
  • [32] Bi-2223 grain growth in Ag/Ni composite-sheathed tapes sintered at different oxygen partial pressures
    Chen, X. P.
    Li, X. G.
    Liu, M.
    Wang, B.
    Liu, Q.
    PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 2015, 212 (08): : 1830 - 1835
  • [33] Processing factors for high critical current density in Bi-2223/Ag tapes
    Willis, JO
    Ray, RD
    Bingert, JF
    Phillips, DS
    Beckman, RJ
    Smith, MG
    Sebring, RJ
    Smith, PA
    Bingham, BL
    Coulter, JY
    Peterson, DE
    PHYSICA C, 1997, 278 (1-2): : 1 - 10
  • [34] Experimental Investigations on the Critical Current of the Jointed Bi-2223/Ag HTS Tapes
    Yan, Zhongming
    Li, Haitao
    Shao, Hui
    Wu, Rui
    Wang, Yu
    JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, 2012, 25 (06) : 1829 - 1832
  • [35] Phase and Texture Evolution of Ag/Ni Composite-Sheathed Bi-2223 Tapes with Different Thickness
    X. P. Chen
    X. W. Yu
    M. Y. Li
    H. B. Sun
    Q. Liu
    Journal of Superconductivity and Novel Magnetism, 2013, 26 : 333 - 336
  • [36] Phase and Texture Evolution of Ag/Ni Composite-Sheathed Bi-2223 Tapes with Different Thickness
    Chen, X. P.
    Yu, X. W.
    Li, M. Y.
    Sun, H. B.
    Liu, Q.
    JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, 2013, 26 (02) : 333 - 336
  • [37] Fabrication and characterization of Ni-clad Bi-2223/Ag superconducting tapes
    Xie, P.
    Qu, T-M
    Song, P.
    Gu, C.
    Huang, K-T
    Han, Z.
    Zeng, P.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2011, 471 (21-22): : 1103 - 1106
  • [38] Microstructure and phase evolution of ultrafine MgO doped Bi-2223/Ag tapes
    Hua, L
    Yoo, J
    Ko, J
    Kim, H
    Chung, H
    Qiao, GW
    PHYSICA C, 1997, 291 (1-2): : 149 - 154
  • [39] Experimental Investigations on the Critical Current of the Jointed Bi-2223/Ag HTS Tapes
    Zhongming Yan
    Haitao Li
    Hui Shao
    Rui Wu
    Yu Wang
    Journal of Superconductivity and Novel Magnetism, 2012, 25 : 1829 - 1832
  • [40] AC losses in superconducting Ag/Bi-2223 composite tapes with interfilamentary barrier
    Ciszek, M
    Tsukamoto, O
    Ogawa, J
    Amemiya, N
    Hayashi, K
    Ueyama, M
    Ayai, N
    PHYSICA C, 2001, 357 (SUPPL. 1): : 1226 - 1229
12345