Vacuum-ultraviolet absorption of amorphous SiO2:: Intrinsic contribution and role of silanol groups

We present a study on the vacuum-ultraviolet (VUV) absorption properties of amorphous SiO(2) (a-SiO(2)) with high concentrations of silanol groups (Si-OH). We found that the absorption spectra are made up of a couple of exponential profiles. The first, in the range from similar to 7.5 to similar to 8.1 eV, was attributed to Si-OH group absorption, while the second, in the range from similar to 8.1 to similar to 8.25 eV, was ascribed to the intrinsic absorption. The VUV absorption cross section of Si-OH groups in a-SiO(2) was determined as well. The intrinsic absorption was found to be affected by the Si-OH concentration: high silanol group contents allow lower values of the Urbach energy. This result is interpreted in terms of a reduction in the degree of disorder in wet materials.