Synthesis and characterization of guar gum-graft-polyacrylonitrile

Cerium(IV) mediated grafting of polyacrylonitrile on to guar gum was studied. Grafting parameters were studied gravimetrically, as a function of temperature, initiator concentration and Guar to acrylonitrile ratio. Higher temperatures resulted in higher monomer conversion and homopolymer formation. Both monomer conversion and extent of grafting increased with increase in cerium ion concentration in the range studied (0.91-9.12 mmol/l). Similar results were obtained with increase in monomer to guar gum ratio from I to 5. Grafting with this initiator was found to be generally good with high grafting efficiencies and low homopolymer formation for most experiments. The copolymers obtained were subjected to alkaline hydrolysis to convert nitrile groups in to carboxylic acid groups and the water absorbency of the resulting anionic guar gum was studied. Materials with water absorption up to 300g/g could be obtained from this study. Copyright (C) 2003 John Wiley Sons, Ltd.