Corrosion resistance of amorphous Fe49.7Cr17.7Mn1.9Mo7.4W1.6B15.2C3.8Si2.4 coating:: A new criticality control material

被引：23

作者：

Farmer, J. C. ^{[1
]}

Choi, J. -S. ^{[1
]}

Saw, C. -K. ^{[1
]}

Rebak, R. H. ^{[1
]}

Day, S. D. ^{[1
]}

Lian, T. ^{[1
]}

Hailey, P. D. ^{[1
]}

Payer, J. H. ^{[2
]}

Branagan, D. J. ^{[3
]}

Aprigliano, L. F. ^{[4
]}

机构：

[1] Lawrence Livermore Natl Lab, Livermore, CA 94550 USA

[2] Case Western Reserve Univ, Cleveland, OH 44106 USA

[3] NanoSteel Co, Idaho Falls, ID 83402 USA

[4] Strateg Anal, Arlington, VA 22201 USA

来源：

NUCLEAR TECHNOLOGY | 2008年 / 161卷 / 02期

关键词：

amorphous metals; iron-based; corrosion-resistant;

D O I：

10.13182/NT08-A3921

中图分类号：

TL [原子能技术]; O571 [原子核物理学];

学科分类号：

0827 ; 082701 ;

摘要：

An iron-based amorphous metal with good corrosion resistance and a high absorption cross section for thermal neutrons has been developed and is reported here. This amorphous alloy has the approximate formula Fe49.7Cr17.7Mn1.9Mo7.4W1.6B15.2C3.8Si2.4 and is known as SAM2X5. Chromium, molybdenum, and tungsten were added to provide corrosion resistance, while boron was added to promote glass formation and the absorption of thermal neutrons. Since this amorphous metal has a higher boron content than conventional borated stainless steels, it provides the nuclear engineer with design advantages for criticality control structures with enhanced safety. While melt-spun ribbons with limited practical applications were initially produced, large quantities (several tons) of gas-atomized powder have now been produced on an industrial scale, and applied as thermal-spray coatings on prototypical half-scale spent-nuclear-fuel containers and neutron-absorbing baskets. These prototypes and other SAM2X5 samples have undergone a variety of corrosion testing, including both salt-fog and long-term immersion testing. Modes and rates of corrosion have been determined in various relevant environments and are reported here. While these coatings have less corrosion resistance than melt-spun ribbons and optimized coatings produced in the laboratory, substantial corrosion resistance has been achieved.

引用

页码：169 / 189

页数：21

共 34 条

[1]

AGARWAL DC, 1997, P CORR 97 NEW ORL LO

[2]

*AM SOC TEST MAT, 1989, 587 ASTM G, P79

[3]

*AM SOC TEST MAT, 1997, 594 ASTM G, P54

[4]

*AM SOC TEST MAT, 1997, 389 ASTM G, P36

[5]

*AM SOC TEST MAT, 1997, ANN BOOK AM SOC TEST, P231

[6]

ASPHAHANI AI, 1980, MATER PERFORMANCE, V19, P33

[7]

BAND AJ, 1980, ELECTROCHEMICAL METH, P67

[8]

BRANAGAN DJ, 2004, PROPERTIES AMORPHOUS

[9] Evaluation of the electrochemical behavior of HVOF-sprayed alloy coatings [J].

Chidambaram, D ;

Clayton, CR ;

Dorfman, MR .

SURFACE & COATINGS TECHNOLOGY, 2004, 176 (03) :307-317

[10]

CHOI JS, 2006, P SCI BAS NUCL WAST, V985

← 1 2 3 4 →