Comparative study of the oxidation and hot corrosion behaviors of TiAl-Cr intermetallic alloy produced by electric current activated sintering

被引：52
作者：
Garip, Y. [1 ]
Ozdemir, O. [1 ]
机构：
[1] Sakarya Univ, Technol Fac, Dept Met & Mat Engn, Esentepe Campus, TR-54187 Sakarya, Turkey
来源：
JOURNAL OF ALLOYS AND COMPOUNDS | 2019年 / 780卷
关键词：
Aluminides; Corrosion; Powder metallurgy; Sintering; HIGH-TEMPERATURE OXIDATION; NB; COATINGS; ENVIRONMENT; ALUMINIDES; PROTECTION; RESISTANCE; SALT;
D O I：
10.1016/j.jallcom.2018.11.324
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Ti-48Al-10Cr (at.%) intermetallic alloy was produced by electric current assisted sintering (ECAS) technique. The oxidation and hot corrosion behaviors of intermetallic alloys were investigated in the cyclic conditions at 700, 800 and 900 degrees C for 180 h in the air. The hot corrosion was realized in the Na2SO4 salt. X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM) equipped with an energy-dispersive spectroscopy (EDS) were used to identify the phase compositions and microstructures of the layers formed on the samples oxidized and hot corroded. The oxidation tests results were showed parabolic behaviors for all test temperatures. In the surface of the corroded samples was observed the separations from porous scale which was composed of Na2Ti3O7, TiO2, Al2O3 and minor phase of TiS. The alloys showed good hot corrosion resistance up to 800 degrees C in the Na2SO4 while the samples showed that weak hot corrosion resistance when the salt was molten at 900 degrees C. In addition, the hot corrosion mechanism was debated on the basis of basic, acidic and synergistic fluxing model. (C) 2018 Elsevier B.V. All rights reserved.
引用
收藏
页码：364 / 377
页数：14
相关论文
共 42 条
[1]   Development of hot corrosion resistant coatings for gas turbines burning biomass and waste derived fuel gases [J].
Bradshaw, A. ;
Simms, N. J. ;
Nicholls, J. R. .
SURFACE & COATINGS TECHNOLOGY, 2013, 216 :8-22
[2]   Welding of yttrium-doped zirconia granules by electric current activated sintering (ECAS): Protrusion formation as a possible intermediate step in the consolidation mechanism [J].
Cordier, Anne ;
Kleitz, Michel ;
Steil, Marlu Cesar .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2012, 32 (08) :1473-1479
[3]   Thermodynamic assessment of the Cr-Ti and first assessment of the Al-Cr-Ti systems [J].
Cupid, Damian M. ;
Kriegel, Mario J. ;
Fabrichnaya, Olga ;
Ebrahimi, Fereshteh ;
Seifert, Hans J. .
INTERMETALLICS, 2011, 19 (08) :1222-1235
[4]   High temperature corrosion mechanisms of certain new TiAl-based intermetallic alloys in an aggressive H2/H2O/H2S environment at 850°C [J].
Du, H. L. ;
Datta, P. K. ;
Hu, D. ;
Wu, X. .
CORROSION SCIENCE, 2007, 49 (05) :2406-2420
[5]   Hot corrosion in gas turbine components [J].
Eliaz, N ;
Shemesh, G ;
Latanision, RM .
ENGINEERING FAILURE ANALYSIS, 2002, 9 (01) :31-43
[6]   Solubility of metal oxides under control of basicity by electrolysis in fused Na2SO4 [J].
Fukumoto, M ;
Suzuki, T ;
Sano, M ;
Hirade, M ;
Hara, M .
MATERIALS TRANSACTIONS, 2004, 45 (10) :2994-2998
[7]   Hot Corrosion Behavior of Ti-48Al and Ti-48Al-2Cr Intermetallic Alloys Produced by Electric Current Activated Sintering [J].
Garip, Y. ;
Ozdemir, O. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2018, 49A (06) :2455-2462
[8]   Reaction morphologies developed by nickel aluminides in type II hot corrosion conditions: The effect of chromium [J].
Gheno, Thomas ;
Azar, Maryam Zahiri ;
Heuer, Arthur H. ;
Gleeson, Brian .
CORROSION SCIENCE, 2015, 101 :32-46
[9]   Synergistic effect of B and Y on the isothermal oxidation behavior of TiAl-Nb-Cr-V alloy [J].
Gong, X. ;
Chen, R. R. ;
Fang, H. Z. ;
Ding, H. S. ;
Guo, J. J. ;
Su, Y. Q. ;
Fu, H. Z. .
CORROSION SCIENCE, 2018, 131 :376-385
[10]   Electric current activated/assisted sintering (ECAS): a review of patents 1906-2008 [J].
Grasso, Salvatore ;
Sakka, Yoshio ;
Maizza, Giovanni .
SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2009, 10 (05)
12345