Preparation and characterization of Sn/La co-doped TiO2 nanomaterials and their phase transformation and photocatalytic activity

The pure, tin (Sn)-doped, lanthanum (La)-doped and Sn/La co-doped titanium dioxide (TiO2) nanomaterials were synthesized using sol-gel method followed by calcination at the temperature of 360 degrees C, 450 degrees C and 600 degrees C, respectively. The structures of the nanomaterials were characterized by X-ray diffraction (XRD), Thermogravimetric (TG), Differential Thermal Analysis (DTA), Scanning Electron Microscopy (SEM), Energy Dispersive Spectrum (EDS), Transmission Electron Microscopy (TEM), X-ray Photoelectron Spectrum (XPS), Diffuse Reflectance Spectrum (DRS), Photoluminescence Spectrum (PL), Brunauer-Emmett-Teller Measurements (BET), respectively. The photocatalytic property of the photocatalysts under UV light was evaluated through the degradation of Rhodamine B (RhB). The results show that the anatase-rutile phase transition is promoted by Sn-doping while La-doping retards the phase transition. However, La doping plays a major role in the process of phase transformation. The photocatalytic activity of pure TiO2 is affected by annealing temperature remarkably and the optimal annealing temperature is 450 degrees C. The photocatalytic activity of TiO2 is enhanced significantly by Sn and La doping at three different temperatures. Sn/La-TiO2 exhibits the highest degradation rates and the fastest reaction rates probably owing to the synergistic effect of Sn4+ and La3+ ions in inhibiting the recombination of photogenerated electron-hole pairs. The formation of extra surface hydroxyl groups and additional surface area are also beneficial for the photocatalytic activity.