Fatigue crack initiation and growth behavior of Ti-6Al-4V under non-proportional multiaxial loading

被引:31
作者
Nakamura, H. [1 ]
Takanashi, M. [1 ]
Itoh, T. [2 ]
Wu, M.
Shimizu, Y.
机构
[1] IHI Corp, Res Lab, Struct Strength Dept, Isogo Ku, Yokohama, Kanagawa 2358501, Japan
[2] Univ Fukui, Grad Sch Engn, Div Mech Engn, Fukui, Japan
关键词
Multiaxial fatigue; Low cycle fatigue; Titanium alloy; Crack nucleation; Fatigue crack growth; LOW-CYCLE FATIGUE; DEFORMATION; STEEL;
D O I
10.1016/j.ijfatigue.2010.12.013
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
This paper deals with multiaxial low cycle fatigue crack behavior of Ti-6Al-4V under non-proportional loading. Strain controlled fatigue tests under proportional loading and non-proportional loading with 90 out-of-phase difference between the axial and shear strains epsilon and gamma were carried out on tubular specimens at room temperature. As a result, Mises strain based fatigue lives under non-proportional loading were approximately 1/10 of those under proportional loading. The specimen surfaces were observed to evaluate life reduction. These results showed that non-proportional loading caused 10 times more cracks than those of proportional loading. Non-proportional loading changes directions of the principal stress and strain axes, and high shear stresses acting on many planes stimulate more slip planes. Consequently, non-proportional loading resulted in many cracks. In addition, the high shear stresses also resulted in larger misorientation under non-proportional loading. The crack initiation life defined as the length 2a of 30 mu m did not differ significantly between proportional loading and non-proportional loading. However, the fatigue cracks under non-proportional loading propagated faster those under proportional loading. This is because the fatigue cracks under non-proportional loading are subjected to more severe strain field than those under proportional loading, even though the crack size and applied strain are the same. Thus, the significant reduction in fatigue life under non-proportional loading is caused by the accelerated crack growth due to a higher strain intensity factor. (C) 2011 Elsevier Ltd. All rights reserved.
引用
收藏
页码:842 / 848
页数:7
相关论文
共 21 条
[1]   Additional cyclic strain hardening and its relation to material structure, mechanical characteristics, and lifetime [J].
Borodii, M. V. ;
Shukaev, S. M. .
INTERNATIONAL JOURNAL OF FATIGUE, 2007, 29 (06) :1184-1191
[2]   Low-cycle fatigue of 1Cr-18Ni-9Ti stainless steel and related weld metal under axial, torsional and 90° out-of-phase loading [J].
Chen, X ;
An, K ;
Kim, KS .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2004, 27 (06) :439-448
[3]  
Chen X, 1999, FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4, P959
[4]   Low-cycle fatigue under non-proportional loading [J].
Chen, X ;
Gao, Q ;
Sun, XF .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1996, 19 (07) :839-854
[5]   DISLOCATION SUBSTRUCTURES AND NONPROPORTIONAL HARDENING [J].
DOONG, SH ;
SOCIE, DF ;
ROBERTSON, IM .
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1990, 112 (04) :456-464
[6]   A CRITICAL PLANE APPROACH TO MULTIAXIAL FATIGUE DAMAGE INCLUDING OUT-OF-PHASE LOADING [J].
FATEMI, A ;
SOCIE, DF .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1988, 11 (03) :149-165
[7]  
GO H, 1999, P 7 INT FAT C, P917
[8]  
Itoh T., 2007, Journal of the Society of Materials Science, Japan, V56, P157, DOI 10.2472/jsms.56.157
[9]   NONPROPORTIONAL LAW CYCLE FATIGUE CRITERION FOR TYPE-304 STAINLESS-STEEL [J].
ITOH, T ;
SAKANE, M ;
OHNAMI, M ;
SOCIE, DF .
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1995, 117 (03) :285-292
[10]  
Itoh T., 1997, 5th Int Conf Biaxial/Multiaxial Fatigue Fract, P173