Metal Temperature Estimation and Microstructure Evaluation of Long-Term Service-Exposed Super304H Steel Boiler Tubes

被引:5
|
作者
Le, Thi Giang [1 ,3 ]
Yoon, Kee Bong [1 ]
Ma, Young Wha [2 ]
机构
[1] Chung Ang Univ, Dept Mech Engn, Seoul 06974, South Korea
[2] Doosan Heavy Ind & Construct, Mat Technol Dev Team, Chang Won 51711, Gyeongnam, South Korea
[3] Thuyloi Univ, Fac Mech Engn, 175 Tay Son, Hanoi, Vietnam
关键词
Super304H steel; Creep; Tube metal temperature; Precipitates; Life assessment; CU-RICH PHASE; HEAT-RESISTANT STEEL; PRECIPITATION BEHAVIOR; STAINLESS-STEEL; M23C6; CARBIDE; MECHANICAL-PROPERTIES; EVOLUTION; CREEP;
D O I
10.1007/s12540-020-00808-4
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The reliability of service-life assessments for the boiler tubes in thermal power plants depends on the prediction of metal temperatures and the evaluation of microstructure changes. Three tubes-one as-received tube and two tubes service-exposed for 54,750 h and 68,550 h-were used to study metal temperature and microstructure characteristics. First, the average metal temperature was estimated (based on accelerated creep rupture test data for the tubes) using the Larson-Miller parameter. The average metal temperature of the tube experienced during its operational period was estimated to be 616 degrees C, which is 16 degrees C higher than the steam temperature of 600 degrees C. Next, the microstructure characteristics were investigated to evaluate precipitation behavior and creep damage. The results demonstrated that the prominent precipitates in the as-received tube sample included coarse primary Nb(C,N) precipitates at the grain boundaries and fine primary Nb(C,N) precipitates (maximum 200 nm) occasionally observed at dislocations. After long-term service, the size and shape of the Nb(C,N) precipitates were relatively stable. In contrast, string M23C6 precipitates and Cu-rich phase particles were identified at the grain boundaries and within the austenitic matrix, respectively. Increasing the aging time from 54,750 to 68,550 h caused strings of M23C6 precipitates to increase rapidly from 60 to 200 nm and the Cu-rich phase particles to increase from 12 to 32 nm. Finally, creep cavities were observed in both service-exposed tubes. However, creep damage characterized by creep cavities that link and grow into microcracks was observed only in the tube sample service-exposed for 68,550 h.
引用
收藏
页码:5121 / 5132
页数:12
相关论文
共 47 条
  • [41] CARBON-STEEL AND 2 1/4CR-1MO STEEL - MECHANICAL AND STRUCTURAL-CHANGES WITH LONG-TERM SERVICE AND REMAINING CREEP LIFE OF BOILER TUBES
    MATSUZAKI, A
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 (05): : S508 - S508
  • [42] OPTIMIZED SPECIFICATIONS FOR TYPE-304 AND TYPE-316 STAINLESS-STEEL IN LONG-TERM HIGH-TEMPERATURE SERVICE APPLICATIONS
    BRINKMAN, CR
    SIKKA, VK
    JOURNAL OF METALS, 1983, 35 (12): : 6 - 37
  • [43] Long-term service evaluation of a pultruded carbon/glass hybrid rod exposed to elevated temperature, hydraulic pressure and fatigue load coupling
    Li, Chenggao
    Yin, Xiaoli
    Liu, Yancong
    Guo, Rui
    Xian, Guijun
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 134 (134)
  • [44] The long-term strength of the metal of steam line tubes made from Cr-Mo-V steel after their service at a thermal power station
    Zlepko, V.F.
    Shvetsova, T.A.
    Linkevich, K.R.
    Teploenergetika, 1999, 46 (05): : 27 - 28
  • [45] Microstructure and Mechanical Property Changes of P92 Steel for Main Steam Pipe in Ultra-supercritical Power Plant After Long-Term Service at High Temperature
    Yong, Li
    Wang, Jiaqing
    Liu, Junjian
    Yue, Wu
    Wen, Fang
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (10) : 4911 - 4919
  • [46] Changes in microstructure of HP-modified, heat-resisting cast alloys under long-term aging. Repair weld cracking of service-exposed, HP-modified, heat-resisting cast alloys (2nd Report)
    Nishimoto, K.
    Saida, K.
    Inui, M.
    Takahashi, M.
    Welding Research Abroad, 2002, 48 (11): : 1 - 9
  • [47] INFLUENCE OF HIGH-TEMPERATURE LOW-CYCLE FATIGUE DEFORMATION ON THE MICROSTRUCTURE OF A CRMOV ROTOR STEEL SUBJECTED TO LONG-TERM SERVICE EXPOSURE AT 425-DEGREES-C AND RETEMPERING AT 677-DEGREES-C
    JOARDER, A
    CHERUVU, NS
    SARMA, DS
    MATERIALS CHARACTERIZATION, 1992, 28 (02) : 121 - 131