Metal Temperature Estimation and Microstructure Evaluation of Long-Term Service-Exposed Super304H Steel Boiler Tubes

被引:5
|
作者
Le, Thi Giang [1 ,3 ]
Yoon, Kee Bong [1 ]
Ma, Young Wha [2 ]
机构
[1] Chung Ang Univ, Dept Mech Engn, Seoul 06974, South Korea
[2] Doosan Heavy Ind & Construct, Mat Technol Dev Team, Chang Won 51711, Gyeongnam, South Korea
[3] Thuyloi Univ, Fac Mech Engn, 175 Tay Son, Hanoi, Vietnam
关键词
Super304H steel; Creep; Tube metal temperature; Precipitates; Life assessment; CU-RICH PHASE; HEAT-RESISTANT STEEL; PRECIPITATION BEHAVIOR; STAINLESS-STEEL; M23C6; CARBIDE; MECHANICAL-PROPERTIES; EVOLUTION; CREEP;
D O I
10.1007/s12540-020-00808-4
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The reliability of service-life assessments for the boiler tubes in thermal power plants depends on the prediction of metal temperatures and the evaluation of microstructure changes. Three tubes-one as-received tube and two tubes service-exposed for 54,750 h and 68,550 h-were used to study metal temperature and microstructure characteristics. First, the average metal temperature was estimated (based on accelerated creep rupture test data for the tubes) using the Larson-Miller parameter. The average metal temperature of the tube experienced during its operational period was estimated to be 616 degrees C, which is 16 degrees C higher than the steam temperature of 600 degrees C. Next, the microstructure characteristics were investigated to evaluate precipitation behavior and creep damage. The results demonstrated that the prominent precipitates in the as-received tube sample included coarse primary Nb(C,N) precipitates at the grain boundaries and fine primary Nb(C,N) precipitates (maximum 200 nm) occasionally observed at dislocations. After long-term service, the size and shape of the Nb(C,N) precipitates were relatively stable. In contrast, string M23C6 precipitates and Cu-rich phase particles were identified at the grain boundaries and within the austenitic matrix, respectively. Increasing the aging time from 54,750 to 68,550 h caused strings of M23C6 precipitates to increase rapidly from 60 to 200 nm and the Cu-rich phase particles to increase from 12 to 32 nm. Finally, creep cavities were observed in both service-exposed tubes. However, creep damage characterized by creep cavities that link and grow into microcracks was observed only in the tube sample service-exposed for 68,550 h.
引用
收藏
页码:5121 / 5132
页数:12
相关论文
共 47 条
  • [21] Microstructure and property of novel heat-resistance steel Super304H after being aged at high temperature
    Li, Xin-Mei
    Zou, Yong
    Zhang, Zhong-Wen
    Zou, Zeng-Da
    Cailiao Gongcheng/Journal of Materials Engineering, 2009, (05): : 38 - 42
  • [22] Effect of Nb on the microstructural evolution and microhardness of Super304H austenitic stainless steel weld metals during long-term aging
    Xiao, Xiaopeng
    Li, Dianzhong
    Li, Yiyi
    Lu, Shanping
    INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2022, 113 (01) : 33 - 43
  • [23] Microstructural evolution of heat-resistant steel Super304H during 650°C long term aging
    Yu, Hong-Yao
    Chi, Cheng-Yu
    Dong, Jian-Xin
    Xie, Xi-Shan
    Cui, Zheng-Qiang
    Chen, Xiao-Fang
    Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing, 2010, 32 (07): : 877 - 882
  • [24] Effect of aging temperature on microstructure and toughness of welded metal of Super 304H steel
    Zhang, Zhongwen
    Li, Xinmei
    Du, Baoshuai
    Zou, Yong
    Wei, Yuzhong
    Hanjie Xuebao/Transactions of the China Welding Institution, 2011, 32 (07): : 43 - 46
  • [25] Intergranular precipitation behavior and its influence on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal during long-term aging
    Xiao, Xiaopeng
    Li, Dianzhong
    Li, Yiyi
    Lu, Shanping
    MATERIALS CHARACTERIZATION, 2021, 178 (178)
  • [26] LONG-TERM CREEP PROPERTIES AND MICROSTRUCTURE OF SUPER304H, TP347HFG AND HR3C FOR ADVANCED USC BOILERS
    Iseda, A.
    Okada, H.
    Semba, H.
    Igarashi, M.
    ADVANCES IN MATERIALS TECHNOLOGY FOR FOSSIL POWER PLANTS, 2008, : 185 - +
  • [27] THE EFFECT OF SIGMA-PHASE FORMATION ON LONG-TERM DURABILITY OF SUPER 304H STEEL
    Horvath, Jakub
    Kral, Petr
    Janovec, Jiri
    Sklenicka, Vaclav
    METAL 2015: 24TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2015, : 505 - 510
  • [28] Effect of long-term exposure at 650 °C on microstructural and creep characteristics of T92/Super304H dissimilar welds
    Nandha Kumar E
    G. D. Janaki Ram
    K. Devakumaran
    Ravi Sankar Kottada
    Welding in the World, 2020, 64 : 467 - 481
  • [29] Effect of long-term exposure at 650 °C on microstructural and creep characteristics of T92/Super304H dissimilar welds
    Kumar, Nandha E.
    Ram, G. D.
    Devakumaran, K.
    Kottada, Ravi Sankar
    WELDING IN THE WORLD, 2020, 64 (03) : 467 - 481
  • [30] Strengthening and Embrittling Mechanism of Super 304H Steel during Long-Term Aging at 650 °C
    Wu, Yue
    Chai, Fufangzhuo
    Liu, Junjian
    Wang, Jiaqing
    Li, Yong
    Du, Chengchao
    MATERIALS, 2024, 17 (03)