Reversible wettability switch of large area TiO2 films

被引：12
|
作者：
Zhou, ZG
Li, FY [1 ]
Song, QL
Yi, T
Hou, XY
Huang, CH
机构：
[1] Fudan Univ, Adv Mat Lab, Shanghai 200433, Peoples R China
[2] Fudan Univ, Natl Key Lab Surface Phys, Shanghai 200433, Peoples R China
来源：
CHEMISTRY LETTERS | 2005年 / 34卷 / 09期
关键词：
D O I：
10.1246/cl.2005.1298
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
On the large area nanoporous TiO2 films with an average pore diameter of 80nm, reversible wettability switch between high hydrophobicity [contact angle (CA) about 137 degrees] and high hydrophilicity (CA < 10 degrees) was achieved by UV light irradiation and dark storage in alternation.
引用
收藏
页码：1298 / 1299
页数：2
相关论文
共 50 条
  • [31] Bioinspired TiO2 Nanostructure Films with Special Wettability and Adhesion for Droplets Manipulation and Patterning
    Lai, Yue-Kun
    Tang, Yu-Xin
    Huang, Jian-Ying
    Pan, Fei
    Chen, Zhong
    Zhang, Ke-Qin
    Fuchs, Harald
    Chi, Li-Feng
    SCIENTIFIC REPORTS, 2013, 3
  • [32] REVERSIBLE PHOTOCONTROL OF WOOD-SURFACE WETTABILITY BETWEEN SUPERHYDROPHILICITY AND SUPERHYDROPHOBICITY BASED ON A TIO2 FILM
    Gao, Likun
    Lu, Yun
    Cao, Jun
    Li, Jian
    Sun, Qingfeng
    JOURNAL OF WOOD CHEMISTRY AND TECHNOLOGY, 2015, 35 (05) : 365 - 373
  • [33] Superhydrophobic Polybenzoxazine/TiO2 Coatings with Reversible Wettability for High-Flux Oil/Water Separation
    Li, Xiu
    Yao, Hongjie
    Lu, Xin
    Xin, Zhong
    INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2021, 60 (23) : 8516 - 8526
  • [34] Voltage-Induced Payload Release and Wettability Control on TiO2 and TiO2 Nanotubes
    Song, Yan-Yan
    Roy, Poulomi
    Paramasivam, Indhumati
    Schmuki, Patrik
    ANGEWANDTE CHEMIE-INTERNATIONAL EDITION, 2010, 49 (02) : 351 - 354
  • [35] Optical and electrical properties of TiO2/Au/TiO2 multilayer coatings in large area deposition at room temperature
    Zhou Jun
    Wu Zhe
    Liu Zhanhe
    RARE METALS, 2008, 27 (05) : 457 - 462
  • [36] Electrochemical fabrication of large-area Au/TiO2 junctions
    Tang, J
    White, M
    Stucky, GD
    McFarland, EW
    ELECTROCHEMISTRY COMMUNICATIONS, 2003, 5 (06) : 497 - 501
  • [37] Optical and electrical properties of TiO2/Au/TiO2 multilayer coatings in large area deposition at room temperature
    ZHOU Jun
    RareMetals, 2008, (05) : 457 - 462
  • [38] Wettability Patternable Hybrid Polymer Films Based on TiO2 and Fluorinated Polymer for Bioelectronics Applications
    Yamamoto, Shunsuke
    Kai, Hiroyuki
    ADVANCED MATERIALS INTERFACES, 2022, 9 (35):
  • [39] Synthesis, structural, photocatalytic, wettability and optical properties of TiO2 films on polymethyl methacrylate substrates
    Hassaballa, S.
    Aljabri, A.
    Mohamed, S. H.
    Hadia, N. M. A.
    Awad, M. A.
    PHYSICA SCRIPTA, 2023, 98 (05)
  • [40] Temperature-dependent differences in wettability and photocatalysis of TiO2 nanotube arrays thin films
    Zhang, Miao
    Yao, Guang
    Cheng, Yunlang
    Xu, Yanyan
    Yang, Lei
    Lv, Jianguo
    Shi, Shiwei
    Jiang, Xishun
    He, Gang
    Wang, Peihong
    Song, Xueping
    Sun, Zhaoqi
    APPLIED SURFACE SCIENCE, 2015, 356 : 546 - 552
12345